Effect of C and Mn element partitioning behavior on microstructure and properties of cold-rolled medium manganese TRIP steel

TIAN Ya-qiang,LI Wang,SONG Jin-ying,WEI Ying-li,DONG Fu-tao,CHEN Lian-sheng
DOI: https://doi.org/10.13228/j.boyuan.issn1001-0963.20180169
2019-01-01
Abstract:The effect of intercritical annealing time on the microstructure evolution, C and Mn elements partitioning behavior, and mechanical properties of ultrafine-grained ferrite and austenite was studied by means of a new heat treatment process of cold rolling followed by warm rolling and intercritical annealing at two-phase region (CR+WR+IA). The results showed that the ultrafine-grained multiphase microstructure composed of ferrite, retained austenite or fresh martensite was obtained after cold-rolled experimental steel treated by intercritical deformation annealing. With prolonging the annealing time at 645 ℃, C and Mn elements constantly diffused from deformed martensite to reverted austenite, resulting in the increase in enrichment sites of C and Mn elements. Meanwhile, recrystallization phenomenon of deformed martensite was obvious in the Mn-rich region. With a small amount of carbide precipitation and dissolution, the yield strength of experimental steel was continuously decreased from 741 to 325 MPa. After intercritical annealing for 10 min, the best comprehensive performance of experimental steel was reached. At this time, the tensile strength reached a maximum value of 1 141 MPa, the elongation after fracture and uniform elongation were 23.6% and 18.1%, respectively, and the product of strength and elongation reached 26.928 GPa·%.
What problem does this paper attempt to address?