Application of waste desulphurization catalyst to iron ore sintering

LIN Chao-yang,ZHU De-qing,GUO Zheng-qi

DOI: https://doi.org/10.13228/j.boyuan.issn1001-0963.20180146

2019-01-01

Abstract:Waste desulphurization catalyst (WDC) is a kind of solid waste generated from coal gas desulphurization process, which contains a certain amount of iron and a large amount of sulfur and calcium. The sinter experiments of WDC blended into iron ores were carried out. The results show that when the ratio of WDC in blends was over 0.1％, with the increase of the WDC, the sinter tumble index, utilization coefficient and reduction degree were decreased, while the concentrations of SO2 and NOx in waste gas were increased, and the low temperature reduction degradation index was improved. Meanwhile, the magnetite mass percent in sinter product was increased, and the mass percent of calcium ferrite was decreased; the morphology changes from needle to columnar and plate shape, and more pores were observed in sinter due to the coarse particles and high sulfur mass percent in WDC. When adding 0.1％ WDC with particle size of-6.3 mm, both the yield and quality of sinter are improved; meanwhile, the mass percents of SO2 and NOx in the flue gas were slightly changed. The industrial test indicated that with less than 0.12％ WDC addition, the quality and yield of sinter are nearly unchanged, and the desulphurization and denitrification of flue gas is hardly affected. Therefore, it is an effective method for resource utilization by adding the WDC into iron ores during sintering process.