Abstract:The corrosion behavior of two types of low-carbon steel (denoted steel A and steel B) in H2S/CO2 was investigated through immersion tests, and the effect of Ti microalloying on the corrosion mechanism was analyzed. The microstructures, corrosion kinetics, corrosion surface morphologies, corrosion phases, cross-sectional morphologies and elemental distributions of the materials were studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron backscatter diffraction (EBSD), energy-dispersive spectroscopy (EDS), x-ray diffraction (XRD) and electron probe microanalysis (EPMA). The results showed that the corrosion rate of steel B with Ti microalloying was lower than that of steel A; the amount and formation rate of corrosion products in these two materials were different. As the immersion time increased, the corrosion products changed from iron-rich mackinawite to sulfur-rich pyrrhotite. In the early stage of corrosion, the corrosion products were primarily mackinawite, which controlled the corrosion phase through the entire process. After 384 h of immersion, pyrrhotite was observed, which can effectively protect the steel substrate, providing excellent corrosion resistance. The corrosion products in steel B with Ti microalloying were more compact than those in steel A. Moreover, Ti enrichment in the oxide film was observed in steel B, which can further improve its corrosion resistance. The results from this study can provide an important reference for the oil and gas industry.

Effect of gas composition on the corrosion behavior of low alloy steel in wet-dry cycling environment

Corrosion Behavior of Low Alloy Steels in a CO2-O2-H2S-SO2 Wet Gas Environment of Crude Oil Tanks

Corrosion Behavior of Low-Alloy Steel in COT Upper Deck O<sub>2</sub>-CO<sub>2</sub>-SO<sub>2</sub>-H<sub>2</sub>S Moisture Environment

Corrosion Behavior of Low-Alloy Steel in Cot Upper Deck O-2-Co2-So2-H2s Moisture Environment

Influence of Chromium on Corrosion Behavior of Low-Alloy Steel in Cargo Oil Tank O2-CO2-SO2-H2S Wet Gas Environment

Effect of H2S concentrations on corrosion failure of L245NS steel in CO2-O2-H2S system

Corrosion Behavior and Kinetics of Early Stages of Low Alloy Steel under H2S/CO2 Environment

Environment corrosion behavior of cargo oil tank deck made of Cr-contained low-alloy steel

Corrosion Behavior of Low-Alloy Steel with Martensite/Ferrite Microstructure at Vapor-Saturated Co2 and Co2-Saturated Brine Conditions

Comparison of Corrosion Behaviors of Low-Alloy Steel Exposed to Vapor-Saturated H2s/Co2 and H2s/Co2-Saturated Brine Environments

Corrosion Behavior of Low Alloy Steel for Cargo Oil Tank under Upper Deck Conditions

Effect of Grain Size on Corrosion Properties of Low Alloy Steel under H2S/CO2 Environment

Corrosion Behavior of Low-Alloy Pipeline Steel Exposed to H2S/CO2-Saturated Saline Solution

Effects of Different Fouling Organisms on Corrosion Behavior of Carbon Steel in Dalian Seawater

Corrosion Behavior of Low‐alloy Steel Used for Pipeline at Vapor‐saturated CO2 and CO2‐saturated Brine Conditions

Effect of SO2 pollution on corrosion behavior of Q235B steel in hot and humid marine atmosphere

Corrosion Mechanism of Low‐alloy Steel Used for Flexible Pipe in Vapor‐saturated H2S/CO2 and H2S/CO2‐saturated Brine Conditions

Research on Corrosion Behavior of Low Alloy Steel Under the Natural Seawater Wet-Dry Alternate Condition

Corrosion Characteristics of Low Alloy Steel under H2S/CO2 Environment: Experimental Analysis and Theoretical Research

Effect of Ti Microalloying on the Corrosion Behavior of Low-Carbon Steel in H2S/CO2 Environment

Effect of Cu and Ni on Corrosion Resistance of Low Alloyed Steels for Cargo Oil Tank