Abstract:Associated with uneven heat transfer in molds, longitudinal off-corner depressions (LOCDs) have been identified as a general defect on wide–thick slabs during continuous casting. Additionally, the concurrent surface and subsurface cracks accompanying LOCDs consistently undermine the quality of high-end steel production. To control LOCDs and crack defects, a multibody and multifield coupling model is developed, upon which a convex-structure mold (CSM) is designed and optimized. In this work, the model is extended to cover the mold, secondary cooling zones, and reduction segments. Thus, the shell deformation can be described during the full process of continuous casting. Based on the model, the CSM is thoroughly compared with a traditional flat-plate mold (FPM) in terms of contact status, air gap expansion, interfacial heat transfer, shell growth, shell deformation, and LOCD formation. The results show that shell shrinkage in the FPM causes a larger contact gap at the corners. Consequently, thick slag layers and air gaps forming around shell corners lead to a hot (thin) spot at the wide face off-corner. With the corner gaps being closed in the CSM, the shell growth at the off-corner is homogenized, and the local hot spot disappears. In secondary cooling zones, the solidifying shell cast by the FPM undergoes larger deformation due to the thin spot. However, uniform shell growth in the CSM could avoid concentrated stress and increase the resistance to deformation. Therefore, the width and depth of the LOCD are greatly reduced throughout the continuous casting process. At the end of mechanical reduction, the depths of the LOCDs in the FPM and CSM cases are 1.77 and 1.1 mm, which correspond to heavy and slight defect levels, respectively. Through these numerical comparisons, the advantages of CSMs in controlling LOCDs are finally confirmed.

Chamfer and Taper Researches of Mould in Slab Continuous Casting

Thermo-mechanical Modeling in Continuous Slab Casting Mould and Its Application

Continuous Casting Mould for Square Steel Billet Optimised by Solidification Shrinkage Simulation

A review of chamfer technology in continuous casting process

Analysis of Thermomechanical Behavior in Continuous Bloom Casting Mold

A Method to Control the Transverse Corner Cracks on a Continuous Casting Slab by Combining Microstructure Analysis with Numerical Simulation of the Slab Temperature Field

Thermomechanical Model of Heat Transffer in Bloom Casting Mold

Heat transfer behaviour of funnel mould copper plates during thin slab continuous casting and channel structure optimization

Thickness Distributions of Mold Flux Film and Air Gap in Billet Ultra-High Speed Continuous Casting Mold Through Multiphysics Modeling

Analysis of Longitudinal Cracking and Mold Flux Optimization in High-Speed Continuous Casting of Hyper-Peritectic Steel Thin Slabs

Numerical Modelling of Chamfer Billet of High Carbon Steel During Continuous Casting

Numerical Study on Characteristic Positions and Transition of Flow Patterns in a Slab Continuous Casting Mold

Numerical Simulation of the Thermo-Mechanical Process for Beam Blank Continuous Casting

A Novel Control Technique for Longitudinal Off-Corner Depressions on Wide Faces of Continuous Casting Slabs: Effect of the Mold Design on Controlling LOCDs

A coupled model on fluid flow, heat transfer and solidification in continuous casting mold

Investigation on non-uniform friction behaviors of slab during continuous casting based on an inverse algorithm

Study on solidification and heat transfer of billet shell in a new-structure high-speed continuous casting mold

Analysis of heat transfer and thermal stress in continuous casting with mechanical reduction

Finite element numerical simulation on Thermo Mechanical couple in bloom mold

Modeling and Simulation of the Fluid Flow in Continuous Slab Casting Mould

Fluid flow and solidification in continuous thin slab casting mold