Hydrometallurgy Asynchronous Recovery of Zinc, Lead and Silver from Pb-Ag Residue

Li Guodong,Lin Hai,Dong Yingbo,Wang Xin,Zhang Yue

DOI: https://doi.org/10.13373/j.cnki.cjrm.XY16050009

2017-01-01

Abstract:In traditional zinc hydrometallurgy process , a large amount of Pb-Ag residue was produced at high temperature acid leac-hing stage.Due to the characteristics of this process , most of the lead and silver metal in zinc concentrate remained in the Pb-Ag resi-due after roasting and acid leaching of zinc concentrate .Although Pb-Ag residue contained high grade of lead and silver , giving its complex mineral composition , relatively fine disseminated particle size of valuable minerals and that the valuable minerals encapsulated by gangue minerals and zinc ferrite , the recovery of valuable metals from Pb-Ag residue was difficult by conventional methods .Thus the method of wet metallurgy was adopted for the recovery of valuable metals from Pb-Ag residue .Asynchronous leaching process was stud-ied by using acid-chlorination leaching to recover zinc , lead and silver .Test results showed that the yield rate of 51.84%for tail residue was obtained with the process as follows .In the acid leaching stage , the conditions were that leaching concentration was 200 g· L-1 , ini-tial acid concentration was 200 g· L-1 , leaching time was 80 min and temperature was 90℃;and in the chlorination leaching stage using the filter residue from the acid leaching , the conditions were that sodium chloride concentration was 300 g· L-1 , leaching concentration was 200 g· L-1 , initial acid concentration was 60 g· L-1 , leaching time was 120 min and temperature was 90℃.Finally, the tail residue contained zinc 0.21%, lead 0.46%, silver 38.50 g·t-1, with the leaching rates of 92.15%, 94.88%, 93.24%, respectively.