Optimization of multi-directional forging parameters of large-scale Mg-Gd-Y-Zn-Zr alloy forged part guided by finite element simulation
Jiyu Li,Jian Zeng,Fulin Wang,Chaoyu Zhao,Haitao Zhou,Fenghua Wang,Shuai Dong,Li Jin,Jie Dong
DOI: https://doi.org/10.1007/s00170-024-13905-0
IF: 3.563
2024-06-15
The International Journal of Advanced Manufacturing Technology
Abstract:Based on the thermal compression stress-strain curves and three-dimensional processing maps of the homogenized Mg-8.5Gd-2.5Y-1.5Zn-0.5Zr (wt%) alloy in our previous published work, we performed a comprehensive investigation to assess the influence of multi-directional forging parameter (i.e. per-pass reduction, pass number and temperature) on the strain uniformity of large-scale forged part by finite element simulation. The results indicate that compared to forging temperature and pass reduction, the pass number of deformation significantly influences the strain uniformity. The optimal forging parameters for a large-scale ingot with 430 mm in diameter and 440 mm in height were obtained, i.e., the forging temperature of 450 °C, pass reduction of 40%, pass number of 5 and forging speed of 10 mm/s. Finally, a large-scale forged part with the diameter of 900 mm and the height of 100 mm was successfully produced under the optimal forming condition. The average grain sizes of edge and center regions of the forged part are (4.08 ± 3.25) μm and (5.58 ± 2.19) μm, respectively, exhibiting a small microstructure difference. The properties are relatively uniform, with the tensile strength differences at each position being less than 20 MPa.
engineering, manufacturing,automation & control systems