Friction, Wear and Corrosion Resistance of Multi-layer Electroless Ni-W-P Coating on AZ91D Magnesium Alloy

Liu Jing,Zhang Tao,Zhang Yuetao,Shao Yawei,Meng Guozhe,Wang Fuhui

DOI: https://doi.org/10.11933/j.issn.1007-9289.20190225001

2020-01-01

Abstract:The multi-layer Ni-W-P electroless coating was successfully prepared on surface of AZ91D magnesium alloy. Microstructure, friction, wear and corrosion resistance of both the normal as-plated and multi-layer coatings were investigated comparatively by XRD, SEM, friction and wear tests, and electrochemical experiments. Results show that the wear coefficient, Vickers hardness and wear rate of multi-layer coating are still keeping the same as those of as-plated coating, which are 0.33, 933 HV. 1.46 mg/Km, respectively. The multi-layer electroless coating completely retains the excellent mechanical properties of the as-plated coating. In addition, the porosity of multi-layer coating is two orders of magnitude lower than that of the ordinary as-plated coating, signifying a denser coating for multi-layer electroless coating. Comparing with the as-plated coating, the corrosion resistance of multilayer coating is improved significantly. The corrosion potential (E-corr) and breakdown potential (E-b) of multi-layer coating are increased by 168 mV and 209 mV respectively, and the passivation current density (i(corr)) is reduced from 4.212 to 1.306 mu A.cm(-2). Therefore, multi-layer electroless coating is expected to be a more promising wear-resistant and corrosion-resistant coating for AZ91D magnesium alloys.