Dependent Effects Of Particle Size On Erosion Wear Mechanism Of Tc4 Titanium Alloy

Geng Ming-Rui,Chen Jiao,Yang Zhu-Fang,Liu Mei-Jun,He Guang-Yu,Wang Xue-De

DOI: https://doi.org/10.11933/j.issn.1007-9289.20180101001

2018-01-01

China surface engineering

Abstract:Using a self-developed air jet erosion experiment platform, an erosion experiment on TC4 titanium alloy with quartz sand in different sizes was performed. The mass loss rate of the erosion, microtography of erosion areas and the stress were measured and analyzed, using a variety of instruments including electronic balance, scanning electron microscope (SEM) and X-ray diffraction (XRD). The results show that the erosion mechanism of TC4 titanium alloy surface is significantly dependent on the particle size and the mechanism changes at 400 mu m. When the particle size is below 400 mu m, the mass loss rate gets less than 0.4 mg/g and plowing, cutting, shoveling and pitting are the main forms of damage in the surface of TC4 titanium alloy. While the particle size is more than 400 mu m, ductile-brittle transition occurs on the surface of TC4 titanium alloy at high strain rate, the mass loss rate suddenly rises above 0.8 mg/g, and cleavage damage and brittle flaking are the main forms of damage. Furthermore, the dual criterion model of cleavage fracture explains the brittle flaking phenomenon on TC4 titanium alloy when the particle size is more than 400 mu m.