Effect of Manganese Dioxide on Acid Leaching of Vanadium from Stone Coal
颜文斌,胡蓝双,高峰,华骏,何新波
DOI: https://doi.org/10.3969/j.issn.0258-7076.2013.01.024
2013-01-01
Abstract:The valence state distribution of +3, +4, +5 V in stone coal from Xiangxi region were 75.67% 17.85% and 6.48%, respectively. Silicate content was higher, it belonged to high silica stone coal mine. Based on the traditional direct acid leaching technology, a small amount manganese dioxide as oxidant was added. Effects of manganese dioxide dosage, liquid-solid ratio, leaching temperature, leaching time, sulfuric acid volume concentration were investigated by single factor experiment and orthogonal test. The results showed that manganese dioxide could coordinate with hydrogen ions to damage the structure of the stone coal and increase significantly the leaching rate of vanadium, and the leaching rate could reach 97.24% under the extraction conditions of oxidant dosage of 2%, liquid-solid ratio of 1:1, leaching time of 13 h, sulfuric acid volume concentration of 25%, leaching temperature of 95°C. Compared with direct acid leaching, the leaching rate increased by more than 40%, compared with traditional roasting technique with sodium chloride, the leaching rate increased by more than 40%, flue gas pollution produced in the roasting process was completely eliminated, the oxidizing acid leaching technology was adopted, without roasting process, not producing flue gas pollution, saving energy, and improving leaching rate of vanadium drastically, realizing the full utilization of the resources, so it had a good application prospect.