Efficient Vanadium Extraction from Shale with High Silicon Content Using a Short Flow Process by Roasting-Water Leaching: Laboratory and Industrial Scale Research

Pengcheng Hu,Yimin Zhang

DOI: https://doi.org/10.1007/s12633-021-01326-7

IF: 3.4

2021-08-19

Silicon

Abstract:With increasing demand for vanadium (V) products in recent years around China, the V utilization from V-bearing shale becomes very important. The V extraction from a shale in Shiyan, Hubei, China was systematically studied. For laboratory experiment, more than 75% of the V can be leached under the experimental conditions of the roasting temperature of 800 °C to 830 °C, the mass ratio of Na2CO3 to NaCl of 7:3–5:5, the composite additive (Na2CO3-NaCl) total dosage of 9 wt.% and the roasting time of 3 h. The microstructure analysis shows that the composite additive can thoroughly destroy structures of silicate minerals (muscovite/illite) during roasting, releasing the V from shale. The phase analysis indicates that albite (NaAlSi3O8) and water-soluble sodium vanadate (NaVO3 and Na4V2O7) were formed during roasting. For industrial test and commercial application, the V leaching efficiency maintained at 80%–85% under the conditions of the roasting temperature of 820 °C–830 °C, the composite additive (Na2CO3-NaCl) total dosage of 9 wt.%, the mass ratio of Na2CO3 to NaCl of 7:3 and the roasting time of 3 h. The NaCl dosage was as low as 2.7 wt.%. More than 99% of the V was recovered in the V precipitation process and the obtained V2O5 product had a purity of 98.2 wt.%-98.6 wt.% in commercial application.

materials science, multidisciplinary,chemistry, physical