Hot Corrosion Performance of Ni Electrodeposited Coatings

MA Li,ZHOU Ke-chao,LI Zhi-you

DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2010.12.016

2010-01-01

Abstract:Ni coatings with different grain sizes,preferred orientation and impurity element contents can be electrodeposited by regulating cathode current density. Using transmission electron microscopy(TEM),scanning electron microscopy (SEM),energy dispersive spectroscopy (EDS) and X-ray diffractometry(XRD),the oxide film structures,composition and morphology of Ni coatings before and after being corroded in corrosive atmosphere of 78.07%Na3AlF6-9.5%AlF3-5%CaF2 (mass fraction,%) were investigated comparatively at 960 ℃. The results show that Ni coatings with smaller grains and a strong 100 preferred orientation are easily obtained under higher current density. While Ni coatings deposited under lower current density have coarser grains and a weak 111 preferred orientation. In the corrosive atmosphere,Ni coating prepared with a lower current density is benefit to the formation of dense NiAl2O4 spinel phase on the surface layer,while NiO is the major phase on the surface of oxide film after the corroding Ni coating prepared with a high current density.