Abstract:Sulfide corrosion cracking of linepipe steel was studied from metallurgical and environmental standpoints using laboratory and full size tests. Sulfide corrosion cracking can be classified into hydrogen induced cracking (HIC) and sulfide stress cracking (SSC). HIC initiates at an elongated inclusion and tends to propagate along microstructural inhomogeneity. The addition of copper was effective in preventing HIC in a relatively mild BP solution, due to the formation of a protective film, but was ineffective in a NACE solution. Calcium treatment of desulfurized steel was effective in preventing HIC initiation. Optimization of the manganese content for controlled rolled plate, and the quenching and tempering process were effective in controlling HIC propagation in a NACE solution. SSC in linepipe steel was closely related with HIC. Measures for HIC were also effective in increasing SSC resistance. Girth welded joints were the most susceptible since SSC occurred at the hardest point in the heat affected zone of the final welding pass. Critical hardness for SSC under the stress level of 1.3 times the yield deflection was Hv 250 and 280 for 1.0 and 0.1 atm partial pressure of H2S gas, respectively. In a full size HIC test simulating an actual pipeline, HIC developed only in the inner side of the steel, resulting in a decrease of the average crack length by one half as compared with laboratory test results. The residual tensile stress of 50 kg/mm2 due to girth welding did not introduce any SSC by itself.

Sulfide Stress Corrosion Cracking Behavior of Low-Cr Steel in H2 S-CO2 Environment

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Corrosion Behavior of Tubing in High-Salinity Formation Water Environment Containing H2S/CO2 in Yingzhong Block

Sulphide Stress Cracking Behaviour of the Dissimilar Metal Welded Joint of X60 Pipeline Steel and Inconel 625 Alloy

Sulfide stress cracking (SSC) of a commercial Q345 pressure vessel steel in a wet H 2 S environment

STRESS CORROSION CRACKING BEHAVIOR OF A NEW KIND OF ULTRAHIGH STRENGTH STEEL Cr12Ni4Mo2Co14 IN ACID ENVIRONMENT

Sulfide Corrosion Cracking of Linepipe for Sour Gas Service

Study on Stress Corrosion Cracking Behavior of Incoloy825/X65 Bimetallic Composite Pipe Welded Joint in Wet Hydrogen Sulfide Environment

Effect of H2S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint

Assessment of sulfide corrosion cracking and hydrogen permeation behavior of ultrafine grain high strength steel

Mechanism of Hydrogen Induced Cracking of Carbon Steel in Simulated Atmospheric Environment Containing SO_2

Combined effect of hydrogen embrittlement and corrosion on the cracking behaviour of C110 low alloy steel in O2-contaminated H2S environment

Effects of H2S/HS− on Stress Corrosion Cracking Behavior of X100 Pipeline Steel Under Simulated Sulfate-Reducing Bacteria Metabolite Conditions

Comparison of 3%-Cr steel and carbon steel corrosion behavior as well tubing materials in CO2–H2S environment

The Effects of NaCl on Hydrogen Permeation and Sulfide Stress Cracking Resistance of C110 High-strength Steel

Influence of H2S on the general corrosion and sulfide stress cracking of pipelines steels for supercritical CO2 transportation

H2S Stress Corrosion Tests of Welded Joint for X65 Pipeline Steel and Finite Element Numerical Analysis of Crack Tip

Stress Corrosion Cracking of 2205 Duplex Stainless Steel with Simulated Welding Microstructures in Simulated Sea Environment at Different Depths

Microstructural Effects in the Development of Near-Neutral pH Stress Corrosion Cracks in Pipelines

Sulfide Stress Cracking Behavior of a Martensitic Steel Controlled by Tempering Temperature

Identifying sulfide stress cracking stages on a HSLA pipeline steel in H2S environment by electrochemical noise