Effect of cryogenic treatment on wear resistance at elevated temperature and dislocation density of tool steel Cr7V

Zhijun Ma,Yi Liu,Binbin Wu,Jianping Lin

DOI: https://doi.org/10.13251/j.issn.0254-6051.2019.01.009

2019-01-01

Abstract:The tool steel Cr7V was treated by quenching at 1030℃for 0.5 h, followed by deep cryogenic treatment at-196℃for 3, 6 and12 h and tempering at 560℃for 2 h by three times.The effect of deep cryogenic treatment parameters on wear resistance of the Cr7V steel was studied by pin-on-disc friction and wear tests.The spectrums of the specimens with different heat treatment parameters were measured by means of XRD.The ray diffraction method was applied to evaluate the dislocation density of the specimens.The results show that the cryogenic treatment has the similar effect on the wear resistance and the dislocation density of the Cr7V steel, with the increase of the holding time, the wear resistance and the dislocation density has a tendency of increasing first and then decreasing.The specimen of cryogenic treated for 6 h and tempering by three times has mass loss of 87.6 mg and dislocation density of 1.4295×1016m-2, the specimen shows the best properties, of which the wear resistance is improved by 53％and the dislocation density is increased by 28％compared with the specimen of conventional treatment.