Evolution Laws of Microstructures and Mechanical Properties During Heat Treatments for Near-Α High-Temperature Titanium Alloys
Ma Xiaozhao,Xiang Zhilei,Li Tao,Chen Yilan,Liu Yingying,Chen Ziyong,Shu Qun
DOI: https://doi.org/10.1007/s12613-021-2248-8
2022-01-01
International Journal of Minerals Metallurgy and Materials
Abstract:Evolution laws of microstructures, mechanical properties, and fractographs after different solution temperatures were investigated through various analysis methods. With the increasing solution temperatures, contents of the primary α phase decreased, and contents of transformed β structures increased. Lamellar α grains dominated the characteristics of transformed β structures, and widths of secondary α lamellas increased monotonously. For as-forged alloy, large silicides with equiaxed and rod-like morphologies, and nano-scale silicides were found. Silicides with large sizes might be（Ti, Zr, Nb） 5 Si 3 and（Ti, Zr, Nb） 6 Si 3 . Rod-like silicides with small sizes precipitated in retained β phase, exhibiting near 45° angles with α/β boundaries. Retained β phases in as-heat treated alloys were incontinuous. 980STA exhibited an excellent combination of room temperature（RT） and 650°C mechanical properties. Characteristics of fracture surfaces largely depended on the evolutions of microstructures. Meanwhile, silicides promoted the formation of mico-voids.