Microstructure control and properties optimization of Ti555211 alloy

AN Zhen,ZHANG Fei-xuan,DENG Fan,JU Xin,DING Xu,WANG Chen,MAO Xiao-nan,ZHANG Ping-xiang

DOI: https://doi.org/10.13289/j.issn.1009-6264.2018-0501

2019-01-01

Abstract:Microstructure and properties of Ti555211 alloy under different heat treatment conditions were studied by means of scanning electron microscopy (SEM) and tensile test. The results show that after solid solution at 800 ℃ for 2 h by air cooling and then aging at 620 ℃ for 8 h by air cooling, the optimum mechanical properties of the Ti555211 alloy can be obtained, and the tensile strength of the alloy is 1315 MPa, the yield strength is 1263 MPa, the elongation and the reduction of area are 14.5％ and 40％, respectively. With the increase of solution temperature, the grain size of the primary α phase decreases from 3.8 μm to 2.8 μm and the primary α phase content decreases from 34.52％ to 20.96％. When the solution temperature continues to increase above the phase transformation point of the alloy, the microstructure of the Ti555211 alloy changes from dual structure to Widmannstatten structure, and the toughness increases.