Effects of pressure on NdCu grain boundary diffusion of Nd-Fe-B sintered magnets

LIU Jian,LI Wei,WANG Qi-xiang,XU Ke,ZHOU Qing,ZHONG Xi-chun,LIU Zhong-wu

DOI: https://doi.org/10.13289/j.issn.1009-6264.2016-X306

2017-01-01

Abstract:Nd70Cu30 eutectic alloy was employed for grain boundary diffusion of commercial N38 magnet with and without pressure.The results show that after the ordinary stress-free grain boundary diffusion,the coercivity of the N38 magnet increased by 14.4％ compared to that of the magnet after the same heat treatment without diffusion,and the coercivity increased by 30.9％ after diffusion under pressure.The microstructure and composition analysis indicate that more discontinuous or continuous Nd-rich grain boundaries appear in the diffused samples,especially in the samples prepared under pressure.Under the pressure,microcracks play an important role as the diffusion channels for Nd-rich liquid phase,which leads to uniformly distributed grain boundary phase in the magnet.As a result,more effectively enhanced coercivity has been achieved.