Study of Microstructure and Mechanical Properties of Ti6246 Pancake Influenced by Forging Temperature

Hongzheng Xie,Guangsheng Xu,Xiaoliang Wang,Jinwen Lei,Yunjin Lai

DOI: https://doi.org/10.13567/j.cnki.issn1009-9964.2017.01.005

2017-01-01

Abstract:Ti6246 alloy bar of φ200 mm× 80 mm was processed into forging pancake.Three forging processes were hired of 985 ℃ (β forging process),935 ℃ (near β forging process) and 900 ℃ (α +β forging process).The results show that microstructure changes obviously during the decrease of the forging temperature.The β forging process is used to obtain the lamellar α phase +β transition microstructure.By using the near β forging process,the structure of spherical α + lamellar α +β transition microstructure is obtained.The α +β forging process is used to obtain the same spherical α phase and β transition structure as the original structure,but the content of the spherical α phase after forging is less.With the decreasing of the forging temperature,the room and high-temperature tensile strength and yield strength of the samples decrease at first and then increase,while plastic property does not change significantly.The high-temperature creep property has no obviously change.Mter thermal exposure 100 h at 427 ℃,the tensile strength and yield strength show a trend of increasing and then decreasing with the decreasing of forging temperature,while plastic property has little changed.