Thermodynamic Investigation of Influence of Substituting Mo for W on Microstructure, Solidification Characteristics and Lattice Misfit of Single Crystal Superalloy

Cheng AI,Yanghui SUN,lin LIU
DOI: https://doi.org/10.14158/j.cnki.1001-3814.2018.08.019
2018-01-01
Abstract:Based on d-electron concept, a W-rich reinforced Ni based single crystal superalloy Alloy W and a Mo-rich reinforced Ni based single crystal superalloy Alloy Mo were designed. The thermodynamic calculation indicates that substituting Mo for Wdecreases the high temperature microstructure stability, liquidus temperature and solidus temperature of γ' phase, while it has small influence on the crystallization temperature range. During the solidification of single crystal superalloy, substituting Mo for W decreases the microsegregation degree of Al element, while the effect on the microsegregation behaviors of Re and Ta elements are not significant. Meanwhile, W and Mo obviously segregate in solidified solid phase and unsolidified liquid phase during the solidification, respectively. Moreover, substituting Mo for W increases the lattice constants of γ phase and γ' phase and then the γ/γ' lattice misfit obviously decreases.
What problem does this paper attempt to address?