Abstract:The chemical compositions of C and Mn have a strong influence on the stability of the metastable retained austenite at room temperature. In the intercritical annealing process, Mn element improves the stability of the austenite by partitioning from ferrite to austenite and the enrichment of Mn in austenite can also impact on the diffusion of C element from martensite to retained austenite in partitioning process. Based on C partitioning, Mn partitioning can further improve the product of strength and elongation, and has no negative effect on weldability of the low carbon high strength steel. Thus, it can effectively solve the contradiction between mechanical property and weldability of low carbon high strength steel in traditional quenching-partitioning (Q&P) process. In this case, it is of great significance to study the Mn pre-partitioning mechanism and its influence on C partitioning and retained austenite of the low carbon high strength steel. Therefore, one low alloy C-Si-Mn steel was studied in the present work. The Mn pre-partitioning behavior and its effect on C partitioning and the stability of the retained austenite were investigated by means of intercritical heating-quenching (IQ) process, Q&P and intercritical heating-austenitizing-quenching-partitioning (I&Q&P) process. The results showed that during the process of phase transformation in the intercritical reheating, C and Mn elements constantly diffused from ferrite to austenite. When this process ended, C and Mn elements enriched in austenite. While Mn element in microstructure at room temperature was still enrichment and C element enriched regularly between the martensite laths in the I&Q&P treated steel. With the increase of C partitioning time in both Q&P and I&Q&P process, the tensile strength of steel was decreased constantly, while the elongation showed an increasing fristly and then decreasing trend. The product of strength and elongation of the steel treated by I&Q&P process reached 23478 MPa % with the C partitioning time of 90 s. The more austenite in martensite phase would be obtained after the first quenching with the Mn pre-partitioning. It was important to prompt more C diffusing into austenite during C partitioning process to stabilize more retained austenite at room temperature of the steel after the second quenching. With the same experimental conditions, the retained austenite of the combined effects of C and Mn partitioning during I&Q&P process would be increased 2.4% than the effect of C partitioning during Q&P process.

Study on Microstructure Evolution of Dual Phase Region and Thermodynamics of C, Mn Partitioning of Low Carbon Si-Mn Steel

Mn Partitioning Behavior of Low Carbon Si-Mn Steel During I & P & Q Process

Experimental and theoretical analysis of multiphase microstructure in a newly designed MnSiCrC quenched and partitioned steel to promote bainitic transformation: The significant impact on mechanical properties

Comprehensive Effect of C,Mn Partitioning Behavior on Retained Austenite of Low Carbon Si-Mn Steel in I&Q&P Process

Microtructure and properties of 0.17C-1.83Mn-1.58Si steel and plasticity enhancement mechanisms of C, Mn partitioning

Effect of Dual-Phase Region Partitioning Temperature on Microstructure and Properties of Low Carbon Steel Containing Copper by I & Q & P Process

Effects of Partitioning Temperature on Microstructure and Properties of C-Si-Mn Steel by Quenching and Partitioning Treatment

Effect of Annealing Temperature and Time on Microstructure Evolution of 0·2c–5mn Steel During Intercritical Annealing Process

Effect of Mn Partitioning Time on Microstructure and Properties of Low-carbon Steel with I&Q&P Treatment

Cu partitioning behavior of Fe-C-Mn-Cu steel by I & Q process

C and Mn Elements Characterization and Stability of Retained Austenite in Different Locations of Quenching and Partitioning Bainite Steels

Effects of Cooling Rate on Microstructure and Mechanical Properties of C-Si-Mn Dual-phase Steel As-hot-rolled

Effects of Mn Partitioning Temperature on Microstructure and Mechanical Properties of Low-Carbon Si-Mn Steel with I & Q & P Treatment

Effect of Partitioning Temperature on Microstructure and Mechanical Properties of C-Mn-Si Steel

Granular bainite microstructure evolution and mechanical properties of low carbon steel in quenching isothermal carbon partition process

EFFECT OF Mn PRE-PARTITIONING ON C PARTITIONING AND RETAINED AUSTENITE OF Q&P STEELS

Element Partitioning Effect on Microstructure and Mechanical Property of the Micro-Laminated Fe–Mn–Al–C Dual Phase Steel

Study on Retained Austenite of Low Carbon Si-Mn Q&P Steel During Partitioning

Analysis of Interface Migration and Isothermal Martensite Formation for Quenching and Partitioning Process in a Low-Carbon Steel by Phase Field Modeling

Microstructure Regulation and Mechanical Properties of Low-Carbon Multiphase Steels

Effect of annealing time on microstructure and mechanical properties of Fe–C–Mn–Al–Si steel