Research on the Microstructure of the Oxidation Film of T91 Steel Tube under the High Temperature and High Pressure Water Vapor

LIU Jiang-nan,ZHAO Yan-fen,GENG Bo,WANG Zheng-pin,YAO Yu-hong,SHI Chong-zhe

DOI: https://doi.org/10.3969/j.issn.1000-8365.2005.03.012

2005-01-01

Abstract:The microstructure and of the oxidation layers of T91 steel tube under the high-temperature and high-pressure water vapor, the profile morphologies of the oxidation film of T91 boiler was observed by the SEM, and the phase structure of the oxide layer was also analyzed by Energy spectrum. The results showed that under high-temperature and high-pressure water vapor the oxide layer of T91 steel tube will produce CrFe_2O_6 on its surface which is single phase structure non-grain boundary non-crystal film ,The film is built up by lots of CrFe_2O_6 which diameter is between 0.1 μm to 0.2 μm, when the Cr、Fe and O is provided enough; And the surface of CrFe_2O_6 will produce CrFe_2O_4 crystal layer. At the begin of the grown of this crytal layer, the rate of (Cr、Fe) to O is constant to the non-crytal layer, but the Cr of CrFe_2O_6 is more than the one of CrFe_2O_4, the Fe of CrFe_2O_6 is less than the one of CrFe_2O_4 .The Fe and Cr will omit 37% in CrFe_2O_4.