Abstract:Because of its extreme hardness, wear resistance, good thermal conductivity and low thermal expansion coefficients, a diamond tool exhibits a range of properties which makes it a key and unique component in many fields of mechanical engineering. In comparison with the other types of diamond tools, the thin film diamond-coated cutting inserts have great potentialities in the commercial application because of its low costs for fabrication equipment and high performance. Thus, they are on the verge of becoming the next generation of tools used for high speed machining non-ferrous metals and alloys, metal-compound materials, and hard brittle non-metals. However, the poor adhesion of the diamond film on the substrate becomes the main technical barriers for the successful development and commercialization of diamond-coated tools. In this paper, diamond thin films were deposited on WC-Co cemented carbide substrates by the electron aided hot filament chemical vapor deposition (EACVD), using a mixture of hydrogen and acetone as source gases. A new multiple chemical pre-treatment including microwave oxidation, reaction in alkaline solution and cleaning by ultrasonic treatment in acid solution has been performed for free shape cemented WC-Co drills in order to increase the diamond nucleation and to enhance the coating adhesion. And also, another new pretreatment method using Ar-HZ gas etching decarburization by microwave plasma is performed for the WC-Co substrate surface. The influences of this pretreatment technique on the adhesion strength, diamond nucleation and surface morphology of the diamond thin film are investigated. Scanning electron microscope (SEM) was used to view the substrate morphology, and to examine the cobalt removal. After pre-treatment, the surface of the WC-Co substrate becomes slightly rough, but its composition and structure shows no changes identified by X-ray diffraction (XRD). Scanning electron microscope (SEM) indicates a distribution of uniform micro-roughness WC grains on substrate surface. And also the research results show that the pretreatment using Ar-H etching decarburization by microwave plasma is an effective method to enhance adhesive strength. The appropriate CVD processes were studied for the fabrication of tools with complex geometries. An adequate amount of additive can effectively prevent the overflow of Co from inner to surface of the substrate and avoid the catalytic effect of Co during CVD. The smooth diamond film with low surface roughness can be deposited by increasing the carbon source concentration and reducing the reactive pressure at the later stage of CVD process. The diamond morphology quality and homogeneity of coatings were characterized by SEM and Raman spectroscopy. The cutting performances of diamond-coated tools were studied by the cutting tests of difficult-to-machine materials. The research results show that the high quality diamond coating has been deposited on complex shape substrates for WC-Co cemented carbide twist drills. The cutting performances of diamond-coated drills are improved further by the new pretreatment and CVD process. It is of great significance for the fabrication and application of the diamond-coated tools with complex geometries.

Process of depositing diamond coating on diamond-impregnated cemented carbide

Study On The Properties Of Diamond Films On Cemented Carbide Substrates By Surface Implantation Pretreatment Process

Study on deposition and characterization of diamond coated cylinder-shaped substrate

Growth and characterization of chemical vapor deposition diamond coating incorporated amorphous carbon with high Raman bands induced by CuO particles

Sandblasting Pretreatment for Deposition of Diamond Films on Wc-Co Hard Metal Substrates

Growth of Nanocrystalline Diamond Films on Co-Cemented Tungsten Carbide Substrates by Hot Filament CVD

Reprint of “A Study of CVD Diamond Deposition on Cemented Carbide Ball-End Milling Tools with High Cobalt Content Using Amorphous Ceramic Interlayers”

Improvement Of Adhesive Strength And Surface Roughness Of Diamond Films On Co-Cemented Tungsten Carbide Tools

Fabrication and application of high quality diamond-coated tools

SiC Interlayer/diamond Coatings Prepared on Cemented Carbide Micro-Tools by High Current DC Extended Arc Chemical Vapor Deposition

The Growth And Interface Characteristics Of Diamond Films On Cemented Carbide Substrates

Effects of Chemical Surface Pretreatments on Diamond Coatings on Cemented Tungsten Carbide Substrate

Interface characteristics of CVD diamond coating on WC-Co cemented carbide substrate

A New Multiple Chemical Pretreatment For Fabrication Of High Quality Cvd Diamond-Coated Drills

Unveiling the formation of Mo2C coating on diamond particles along with anisotropic etching by Mo powder

Deposition of Diamond Films on Smooth Surfaces of Cemented Carbide Inserts with Cobalt Boride Interlayers

Design and Fabrication of HfC, SiC/HfC and HfC-SiC/HfC Interlayers for Improving the Adhesion Between Diamond Coatings and Cemented Carbides

A competitive-adsorption chemical vapor deposition method: Diamond coated on WC-Co substrate without acid-alkali pretreatment by adding graphene oxide particles

Deposition and Characterization of Nanocrystalline Diamond Films on Co-cemented Tungsten Carbide Inserts

Preparation of Ti-coated Diamond Particles by Microwave Heating

Advances in deposition of diamond films on cemented carbide and progress of diamond coated cutting tools