Experimental Study on Creep Properties of Local Zones in a Weld Metal Produced by Multi-pass Welding of Thick-walled Pipes

YANG Bin,LIU Xin-ping,XUAN Fu-zhen
DOI: https://doi.org/10.3969/j.issn.1001-4837.2016.10.001
2016-01-01
Abstract:Creep test with micro-specimens were conducted to study the properties of local zones in a heat resistant steel weld metal produced by multi-pass welding.The relationship between fracture morphology and microstructure of creep ruptured specimens was investigated.Results shown that different creep prop-erties can be clearly observed in local zones in multi-pass weld metal.The creep strength of specimen lo-cated in the weld pass parallel to welding direction has a maximum value,followed by that through multi-ple weld passes,and that located in the weld pass overlap perpendicular to welding direction.Meanwhile, the corresponding creep crack initiation sites are coarse grain zone,columnar grain zone and recrystallized grain zone,respectively.The above difference among local zones can induce the variation of the deforma-tion amplitude during primary and secondary creep stages,while it nearly has no effect on deformation law.The composition of specimen may be different as sampling location changes,while the applied stress on local zones may be different even for the same load when sampling direction changes.Both of them lead to macroscopic anisotropic creep behavior of multi-pass weld metal.
What problem does this paper attempt to address?