Dynamic Mechanical Behaviors of a Short-glass-fiber Reinforced Polyamide in Hopkinson Bar Test

Yan-pei WANG,Qi-fan JIANG,Yu-long LI

DOI: https://doi.org/10.3969/j.issn.1000-1093.2018.01.018

2018-01-01

Abstract:To investigate the dynamic mechanical property of a 50％ short-glass-fiber reinforced polyamide,the quasi-static hydraulic testing machine and split Hopkinson pressure/tension bar are used to apply loading on specimens with diameters from 6 mm to 10 mm,and the average strain rate is between 0.000 5 s-1 and 1 600 s-1.The stress-strain curves and failure modes of specimens are obtained and investigated.Micro-mechanics of failure process at different strain rates are analyzed.It can be seen from the stress-strain curves that the strength of material under dynamic loading are obviously higher than that under quasi-static loading (the compression strengths are increased by 31％,25％ and 29％ at the strain rates of 400 s-1,900 s-1 and 1 600 s-1,respectively;and the tensile strengths are increased by 46％,47％ and 28％ at the strain rates of 400 s-1,800 s-1 and 1 200 s-1,respectively),and the failure strain decreases significantly.The failure processes at different strain rates are also investigated.Under compression loading,the specimens experience the compaction of existing defect,elastic deformation and failure;under tensile loading,the specimens experience only elastic deformation and failure.The growth processes of micro-cracks are obviously different under static loading and quasi-static loading:under quasi-static loading,the micro-cracks assembly into macro-cracks.On the contrary,micro-cracks separately grow into macro-cracks.Optical observation and scanning electron microscope (SEM) are adopted to investigate the fracture surface.Results show that the fiber pull-out and fiber fracture are generated under dynamic compression,the fracture surface are smoother under quasi-static compression.And under tensile loading,dynamic surface shows fiber fracture,and quasi-static surface shows fiber pull-out.