Synthesis and Chemical Stability of LaMgAl11O19 Ceramic Materials for the Lattice Solidification of High Level Radioactive Waste

Hao-ran LU,Chang-an WANG

DOI: https://doi.org/10.3969/j.issn.0258-0918.2017.06.016

IF: 1.2

2017-01-01

Nuclear Science and Engineering

Abstract:The solidification of high level radioactive waste is the first safety barrier to prevent radioactive radioactive waste proliferating.Due to high inclusion,high density,low leaching rate and anti-irradiation stability,magnetoplumbite-type LaMgAl11O19 are selected as the most promising new generation lattice solidification ceramic materials,which could overcome the inherent technology defects of glass solidification in the backend of the nuclear fuel cycle.The LaMgAl11O19 ceramic materials were prepared by citric acid sol-gel chemical processing,the chemical composition,micromorphology and electron diffraction pattern were characterized by X-ray diffraction,scanning electron microscope and high resolution transmission electron microscope/selected area electron diffraction,respectively.The component,micromorphology and ant-deliquescence properties were analyzed before and after soaking in deionized water.The results indicate that LaMgAl11O19 ceramic materials have pure hexagonal magnetoplumbite crystal structure,the average crystalline grain size of the samples sintered at 1 500 ℃ for 4 h was 89.4 nm which calculated by Scherrer formula and micromorphology.The bivalent Mg2+ cation dissolving-out of [MgO4] lattice result in the deliquescence and structural instability.This paper provides a theoretical basis for the commercial application of candidate lattice solidification materials which used to high level radioactive waste.