The Effect of Waste Loading on Phase Composition, Structure and Chemical Durability of Glassy Materials for Immobilization of High-Sodium/Aluminum Waste-11475

G. A. Malinina,S. V. S. A. S. Sorokaletova

Abstract:Mixtures of surrogates of high level waste with high sodium and aluminum contents and sodiumlithium borosilicate frit were placed in alumina crucible, heated to 1200-1300 °C depending on waste to frit ratio in a resistive furnace and kept at melting temperature for 1 hr. Portions of melts were poured onto a metal plate (quenched) and the residues were slowly cooled in turned-off furnace (annealed). The quenched materials contained up to 45 wt.% waste oxides were fully amorphous whereas in the materials with higher waste loadings minor spinel structure phases occurred. The annealed materials with waste loading of up to 45 wt.% contained minor spinel type phase and trace of nepheline (Na,K)AlSiO4. In the annealed materials contained waste oxides in amount of 50 wt.% and more nepheline and spinel were found to be major and minor phases, respectively. Two spinel varieties – first and second generation different in crystal size and geometry occurred. The materials at 55, 60 and 65 wt.% waste loadings are nearly fully crystalline and contain, except nepheline and spinel, extra Cs-bearing phases. These phases coexist with nepheline and their chemical compositions are recalculated to formulae with 4 oxygen ions. One of them contains up to 0.30 Cs and 0.13 S ions per formula, chemical composition of the second one is close to CsAlSiO4. Chemical durability of the materials worsens with waste loading but even at waste loading of 55 wt.% normalized releases of B, Li, Na and Si from the material determined using PCT procedure remain lower than those from EA glass.

Environmental Science,Materials Science