Influence of Crosslinking by-products on Dielectric and Mechanical Properties of XLPE Cable Insulation

Benhong Ouyang,Jiankang Zhao,Huan Li,Jianying Li
DOI: https://doi.org/10.3969/j.issn.1009-9239.2015.05.008
2015-01-01
Abstract:In view of the problem that the crosslinking by-products decomposed by dicumyl peroxide (DCP) when 110kV XLPE cable is crosslinking would affect the property of cable, XLPE cables were degassed, and the degassed cables insulation were tested by FTIR, then their dielectric property and mechanical properties before and after degassing were analyzed. The results show that the content of two volatile crosslinking by-products, which are methyl styrene and acetophenone, reduce significantly during degassing process, which lead to the quantity of polar groups and conductivity at low frequency decrease, thereby the relative dielectric constant and dielectric loss factor at low frequency of XLPE decrease, and the tensile strength and elongation at break increase.