Facile and Scalable Fabrication of High-Performance Microsupercapacitors Based on Laser-Scribed In Situ Heteroatom-Doped Porous Graphene
Min Yuan,Feng Luo,Zeping Wang,Hui Li,Yifan Rao,Jiabing Yu,Ying Wang,Dingli Xie,Xianping Chen,Ching-Ping Wong
DOI: https://doi.org/10.1021/acsami.1c03219
2021-05-07
Abstract:This study proposes an efficient, facile, and scalable strategy to synthesize <i>in situ</i> heteroatom-doped porous graphene via laser direct writing on the precursor-doped polyimide (PI) film, which is fabricated for the first time through incorporating PI powder and precursors with sodium carboxymethyl cellulose (CMC) binder by a drop-casting and low-temperature drying process. The resulting microsupercapacitors (MSCs) based on the as-prepared heteroatom-doped porous graphene exhibit remarkable capacitive performance. The typical boron-doped MSC prepared on borax-doped polyimide film possesses an ultrahigh areal capacitance of 60.6 mF cm<sup>–2</sup> at 0.08 mA cm<sup>–2</sup>, which is approximately 20 times larger than that of undoped MSC. Furthermore, the boron-doped MSC has impressive cycling stability (with the capacitance retention of 96.3% after 20 000 cycles), exceptional mechanical flexibility, tunable capacitance, and voltage output through arbitrary modular serial and parallel integration. Besides, the nitrogen-doped porous graphene with excellent capacitive performance is also prepared by laser direct scribing on the sulfonated melamine-doped polyimide film, demonstrating excellent scalability and generality of this strategy. Hence, one-step laser direct writing on precursor-doped polyimide films can realize <i>in situ</i> heteroatom doping and generation of hierarchical porous graphene electrodes simultaneously, which opens a new avenue for the facile, cost-effective, and scalable fabrication of heteroatom-doped porous graphene, thus promising for MSCs and various flexible and wearable electronics at large-scale production.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c03219?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c03219</a>.Experimental section (materials characterization, electrochemical performance calculations, DFT calculations); photographs of LIG-B6 on PET, PMMA, and fabric substrates; SEM and TEM images of pure LIG electrodes; cross-sectional SEM images of LIG, LIG-B6, and LIG-N6 electrodes; pore size distribution of LIG and LIG-B6; Raman spectrum and a photograph of the PI/CMC film; C 1s, B 1s, and O 1s XPS speaks of LIG-B<i>x</i> samples; sheet resistance and conductivity of LIG-B<i>x</i> films; CV curves at scan rates from 10 to 200 mV s<sup>–1</sup> and GCD curves at current densities from 0.08 to 1 mA cm<sup>–2</sup> of LIG-B0, LIG-B4.5, and LIG-B7.5; SEM image of LIG-B7.5; water contact angles of LIG, LIG-B6, and LIG-N6; adsorption energy calculated by DFT of LIG-B6; volumetric capacitance and areal and volumetric Ragone plots of LIG-B<i>x</i>; pore size distribution and Raman spectra of LIG-N<i>x</i>; sheet resistance and conductivity of LIG, LIG-B6, and LIG-N6; GCD curves at current densities from 0.08 to 1 mA cm<sup>–2</sup> of LIG-N3 and LIG-N9; atomic ratios of LIG-B<i>x</i>; and comparison of capacitive performance of LIG-B6 with other MSCs (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c03219/suppl_file/am1c03219_si_001.pdf">PDF</a>)Three LIG-B6 MSCs connected in series light a timer (Video S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c03219/suppl_file/am1c03219_si_002.mp4">mp4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology