Abstract:Resolving severe deactivation by alkali metals for selective catalytic reduction of NOx with NH3 (NH3-SCR) is challenging. Herein, surface Ce2(SO4)3 species as a self-protection armor originally exhibited antipoisoning of potassium over ceria-based catalysts. The self-protection armor was also effective for other alkali (Na), alkali-earth (Ca), and heavy (Pb) metals, considerably resolving the deactivation of ceria-based SCR catalysts in practical applications. The catalytic activity tests indicated that the presence of ∼0.8 wt % potassium did not deactivate sulfated CeO2 catalysts, yet commercial V2O5-WO3/TiO2 catalysts almost lost the NOx conversions. Potassium preferably bonded with surface sulfates to form K2SO4 accompanied with the majority of surface Ce2(SO4)3 over sulfated CeO2 catalysts, but preferably coupled with active vanadia to generate inactive KVO3 species over V2O5-WO3/TiO2 catalysts. Such an active Ce2(SO4)3 species facilitated the adsorption and reactivity of NH3 and NOx, enabling ceria catalysts to maintain high catalytic efficiency in the presence of potassium. Conversely, the introduction of potassium into V2O5-WO3/TiO2 catalysts caused a considerable loss of surface acidity, hindering catalyst reactivity during the SCR reaction. The self-protection armor of Ce2(SO4)3 species may open a promising pathway to develop efficient ceria-based SCR catalysts with strong antipoisoning ability.

Alkali metal(potassium)poisoning mechanism of CeFeOx catalysts for selective catalytic reduction of NOx

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

The Influence of Alkali Metals on the Ce‐Ti Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx

Unraveling Alkali-Tolerance Role of Zeolite Coupling CeWOx Catalyst for NOx Reduction

Poisoning Mechanism of Alkali Metal on Cu–Fe2O3 Catalyst for Selective Catalytic Reduction of NO with NH3

Alkali Metal Poisoning of A Ceo2-Wo3 Catalyst Used in the Selective Catalytic Reduction of Nox with Nh3: an Experimental and Theoretical Study

Poisoning Effects of Alkali and Alkaline Earth Metal Doping on Selective Catalytic Reduction of NO with NH3 over the Nb-Ce/Zr-PILC Catalysts

Deactivation Mechanism of Potassium on the V2o5/Ceo2 Catalysts for Scr Reaction: Acidity, Reducibility and Adsorbed-Nox

Alkali-resistant Catalytic Reduction of NO over CeO2-WO3/MCM-22 Supported Catalyst by Releasing Brønsted Acid Sites

Potassium Poisoning Impact on FeCu Selective Catalytic Reduction Catalyst: Structure and Mechanism

Alkali poisoning of Fe-Cu-ZSM-5 catalyst for the selective catalytic reduction of NO with NH3

Acidified SiO2 Supported Fe-based Bimetal Oxide Catalyst with Resistance to High-Level Alkali Poisoning for CO Selective Catalytic Reduction of NO Removal of NOx

Efficient NO x Reduction against Alkali Poisoning over a Self-Protection Armor by Fabricating Surface Ce2(SO4)3 Species: Comparison to Commercial Vanadia Catalysts

The Poisoning Effect of KCl and K2O on CeO2-TiO2 Catalyst for Selective Catalytic Reduction of NO with NH3

Regeneration of Potassium Poisoned Catalysts for the Selective Catalytic Reduction of NO with NH3

Poisoning of Mn-Ce/AC Catalysts for Low-Temperature NH3-SCR of NO by K+ and Its Counter-Ions (Cl−/no3−/so42−)

Efficient NOx Reduction Against Alkali Poisoning over a Self-Protection Armor by Fabricating Surface Ce2(SO4)3 Species: Comparison to Commercial Vanadia Catalysts

Superior PbO-resistance of CeO2/ZrO2 catalyst promoted by solid superacid SO42−/ZrO2 for selective catalytic reduction of NOx with NH3

Superior PbO-resistance of CeO2/ZrO2 Catalyst Promoted by Solid Superacid SO42−/ZrO2 for Selective Catalytic Reduction of NO with NH3

Insight into the Alkali Resistance Mechanism of FeMoTiOx Catalysts for NH3 Selective Catalytic Reduction of NO: Self-Defense Effects of MoOx for Alkali Capture.

Low temperature selective catalytic reduction of NO with NH3 over CeFeOx catalyst