Optical Properties and Thermal Stability of Infrared Chalcogenide Glass Ga2S3-Sb2S3

Ge LI,Tiefeng XU,Shixun DAI,Tengyu ZHANG,Qinyuan ZHANG,Qing JIAO

DOI: https://doi.org/10.14062/j.issn.0454-5648.2016.06.08

2016-01-01

Abstract:Series of GaxSb40–xS60 chalcogenide glasses were synthesized by a melt-quenching method. The thermal and optical properties of sample glasses were determined by the Archimedes principle, X-ray diffraction, thermal expansion, ultra violet–visible–near infrared absorption spectroscopy, and Fourier transform infrared spectroscopy, respectively. The structures of the samples with different compositions were analyzed by Raman spectroscopy. The results show that all of the glasses have good thermal stability and spectral properties. The density decreases slightly, the glass transition temperature improves, and the thermal expansion coefficient reduces with increasing the content of gallium. Besides, there is a slightly augmentation of optic band gap and a regularly blue-shifted of IR absorption cutting-off edge. Since all of the chalcogenide glasses have a high transmittance in a wide spectrum range of 0.8–14 μm (covering three main commutation bands and thermal infrared band), they are thus a promising material for mid-infrared application. According to the Raman spectra, the formation of [GaS4] tetrahedral units promote and the [SbS3] pyramid units suppress with the increase of gallium content. The relationship between optical properties and the structure in the chalcogenide glasses was summarized.