Abstract:The full exposure of active ingredients plays an important role in the enhancement of catalytic performance. In this work, a series of novel catalysts, Mn-Co mixed oxide nanosheets with ultrathin thickness (about 3.5nm) and different Mn/Co ratios (0.52, 0.69, and 1.52) vertically anchored on a support (H2Ti3O7 nanowires), are rationally developed. This unique structure not only fully exposes the active ingredients of the Mn-Co mixed oxides, but also is very favorable for the diffusion and transfer of gas molecules through the space between these standing nanosheets. As expected, the developed catalysts (MnOx-CoOy/H2Ti3O7, MnCoTi), especially MnCoTi-2 with the Mn/Co molar ratio of 0.69, present excellent low-temperature selective catalytic reduction (SCR) performance, high N-2 selectivity, superior water tolerance and stability. The relative turnover frequency (TOF) value over MnCoTi-2 at 100 degrees C is as high as 9.25x10(-4)s(-1) under the gas hourly space velocity (GHSV) of 200000h(-1), which is rarely reported among Mn-Ti, Mn-Co, and Mn-Co-Ti mixed oxide catalysts. The results of in situ diffuse reflectance infrared Fourier transform spectroscopy suggest that the coordinated NH3, NH4+ ions, adsorbed NO2, and bidentate nitrate are the reactive species and the Eley-Rideal and Langmuir-Hinshelwood mechanisms can be simultaneously involved on the surface of the MnCoTi-2 at a relatively low temperature (90 degrees C).

STRUCTURAL AND HYDROGEN TEMPERATURE PROGRAMMED REDUCTION PROPERTIES OF MCM- 41 SUPPORTED COPPER OXIDE CATALYSTS

The Selective Catalytic Reduction Activity of Cu/MCM-41 Catalysts Prepared by Using the Cu2+–MCM-41 Mesoporous Materials with Copper Ions in the Framework As Precursors

Synthesis of hierarchically structured MCM-41 with high hydrothermal stability and its application in environmental catalysis

The Synergistic Effect of Bimetallic Zn-Ti in Mcm-41 Support for the Improvement of Catalytic Activity

Preparation and Catalytic Properties of Fe-Ti-Mcm-41

Preparation, Characterization and Desulfurization Performance of Cu/Ti-MCM-41 and Cu/Ti-HMS Catalysts

EFFECT OF CALCINATION TEMPERATURE ON THE STRUCTURE AND CATALYTIC PERFORMANCE OF THE CU-MCM-41 CATALYSTS FOR THE SYNTHESIS OF DIMETHYL CARBONATE

Studies of Pore Structure, Temperature-Programmed Reduction Performance, and Micro-Structure of CuO/CeO2 Catalysts

Catalysts from MCM-41: framework modification, pore size engineering, and organic–inorganic hybrid materials

Investigation of the Structure of MCM‐41 Samples with a High Copper Content

Mn−Co Mixed Oxide Nanosheets Vertically Anchored on H2Ti3O7 Nanowires: Full Exposure of Active Components Results in Significantly Enhanced Catalytic Performance

Catalytic performance of Cu-MCM41 with high copper content for NO reduction by CO

Benzaldehyde reduction over Cu-MCM-41 catalyst: Influence of the Si/Cu ratio during hydrothermal synthesis on the structure and catalytic properties

Controllable in Situ Surface Restructuring of Cu Catalysts and Remarkable Enhancement of Their Catalytic Activity

Enhancing Sintering Resistance of Atomically Dispersed Catalysts in Reducing Environments with Organic Monolayers

Studies on the Tpr Characteristics and Oxidation Activities of Catalysts of Cu,Ag and Cu-Ag Supported on Gamma-Al2o3

A composite having a porous substrate and polyhedral Cu-Fe oxide nanoparticles showing high catalytic activity during the steam reforming of methanol at low temperatures

Activation of MCM-41 mesoporous silica by transition-metal incorporation for photocatalytic hydrogen production

In-situ fabrication of Cu-Mn-O nanostructure catalysts on Ti mesh and their catalytic property optimization for low-temperature and stable CO oxidation

Enhancing the Low-Temperature CO Oxidation over CuO-Based -MnO<sub>2</sub> Nanowire Catalysts

Oxidation–Reduction Treatment Initiated in Situ Redispersion of the Supported Cu/Al2O3 Catalyst