Mechanism study on SO2 poisoning of FexMnCe1-AC catalyst for low-temperature SCR

Xiaoxue CHEN,Min SONG,Fanyue MENG,Yuexing WEI

DOI: https://doi.org/10.11949/0438-1157.20190318

2019-01-01

Abstract:A series of FexMnCe1-AC catalysts were prepared by ultrasonic-assisted impregnation method with activated carbon as carrier. The low-temperature NH3-SCR denitrification activity of the catalysts was investigated, and the best activity catalyst was established. The effect of SO2 on its denitration performance was also explored. The results showed that Fe0.1MnCe1-AC catalyst exhibited best denitration efficiency at low-temperature among prepared catalysts, the conversion rate of NO exceeded 90% with the temperature range from 120℃ to 220℃ (no SO2). In addition, the catalyst could maintain NO conversion rate of approximately 77% under the atmosphere of 180℃and SO2 concentration of 429 mg/m3. The mechanism of SO2 poisoning on the catalyst was characterized with BET, XRD, XPS, H2-TPR NH3-TPD, FT-IR and TGA. It was observed that SO2 could form ammonium sulfate ( (NH4)2SO4, (NH4)2SO3 ), and MnSO4 with NH3 and the metal components in the catalyst, which changed the pore structure of the fresh catalyst and reduced the Br?nsted acid sites and Lewis acid sites on the catalyst surface. These variation made the inhibitory effect on the catalytic adsorption capacity of NH3. Moreover, SO2 also promoted a decrease in the number of Mn4+, Ce3+, Fe3+and Fe3+—OH-groups in the catalyst, and lessened the surface reducible species, thereby reducing the activity of the catalyst denitration.