Synthesis and Properties of Water Dispersive SiO2@PANI Anticorrosion Materials

Xiao-hui GAO,Xiao-yan JING,Yu-feng LI,Jing-jing ZHU,Shi QI

DOI: https://doi.org/10.13550/j.jxhg.2017.04.003

2017-01-01

Abstract:Polyaniline(PANI) grafting silica(SiO2)(SiO2@PANI) sol was firstly synthesized by a grafting reaction between aniline and SiO2 sol modified by γ-glycidoxypropyltrimethoxysilane(GPTMS),and then the resulting SiO2@PANI sol was in situ embedded with vinyl trimethoxysilane(VTMS) to afford SiO2@PANI/VTMS composite sol.The effects of reaction temperature and dosage of initiator on the dispersion stability and particle size of SiO2@PANI sol,as well as contact angle and corrosion resistance of the coatings were discussed.The structure and morphology of SiO2@PANI particles were characterized by Fourier transform infrared(FTIR) spectroscopy and scanning electron microscopy(SEM).The results showed that GPTMS modified SiO2 could promote the uniform polymerization of aniline on the surface of SiO2 by the reaction between the amino group and epoxy group.The core-shell type SiO2@PANI sol was obtained using SiO2 and PANI as core and shell,respectively.The SiO2@PANI sol exhibited good water dispersion stability when the reaction temperature is 10 ℃ and n(APS)/n(An)=0.75,and conductivity is up to 3.8×10-2 S/cm.The prepared SiO2@PANI/VTMS composite sol could form hydrophobic coatings by coating it on the surface of magnesium-lithium(Mg-Li) alloy directly,and the water contact angle of the composite coating reached 135.7°.In addition,the coating exhibited an excellent corrosion resistance performance to Mg-Li alloy,the electrochemical impedance value was 2.3×104 Ω·cm2 and the corrosion current density was only 7.51×10-7 A/cm2.