Abstract:Polyaniline (PANI) particles were synthesized using aniline (AN), dodecyl benzene sulfonic acid (DBSA), and ammonium persulfate (APS). The particles were analyzed using scanning electron microscope (SEM), X‐ray diffraction (XRD), and fourier transform infrared spectroscopy (FTIR). A PANI/waterborne polyurethane composite material (PANI‐WPU) was obtained by combining it with polyethylene glycol (PEG600), diphenylmethane diisocyanate (MDI), dimethylol propionic acid (DMPA), N‐methyl pyrrolidone (NMP), and dibutyltin lauric acid (DBTDL). The structure was characterized by the FTIR spectrum. The mechanical characteristics of the coating film were evaluated with respect to the PANI content, as well as its water absorption, glossiness, electrochemical corrosion resistance, and acid and alkali resistance. The PANI/waterborne polyurethane film has a maximum tensile strength of 23 ±1 MPa, an elongation of 1012%, a pencil hardness of 5H, a flexibility of 2 mm, an impact resistance of 50 cm, the water absorption of 14.66%, and the glossiness of 99.9 ±0.1 at 60°. When the PANI content is 0.7%, the mechanical characteristics, glossiness, and anti‐corrosion performance of the composite film improve. The corrosion inhibition efficiency of the aqueous polyurethane coating film with PANI can reach 99.74%, as shown by the examination of electrochemical polarization curves and impedance spectra. The tinplate is coated with a 0.7% PANI‐WPU composite material and edge sealing. This coating provides excellent protection against acid and alkali resistance, as demonstrated by its ability to withstand immersion in 10% H2SO4 and 10% NaOH solution for 90 days without any paint peeling off.

Preparation and Properties of Silicon Dioxide/Polyaniline Composite Particles

Preparation of Polyaniline Doped with Acid and Polymer Using Electrochemical Deposition

Preparation and Properties of Polyaniline–anionic Spherical Polyelectrolyte Brushes Nanocomposite

Effects of Acidity on the Size of Polyaniline-Poly(sodium 4-Styrenesulfonate) Composite Particles and the Stability of Corresponding Colloids in Water

A Very Thin Layer of NiO, Ni(OH)2 Nanosheets Arrays with Organic Functional Modification of Polyaniline

Preparation of polystyrene/polyaniline core/shell structured particles and their epoxy-based conductive composites

Syntheses and Properties of Polyaniline Coated Polystyrene Particles

Synthesis of Polyaniline/mcm‐41 Composite Through Surface Polymerization of Aniline

Preparation and corrosion resistance of polyaniline and waterborne polyurethane composite coating film

Preparation and anti‐corrosion performance of nano Polyaniline/Polyurethane interpenetrating network composite coating

Iron-Oxide-Nanoparticles-Doped Polyaniline Composite Thin Films

Synthesis and Properties of Water Dispersive SiO2@PANI Anticorrosion Materials

Controlling the Morphology of Micrometre-Size Polystyrene/polyaniline Composite Particles by Swelling–Diffusion–Interfacial-Polymerization Method

Preparation of polyaniline‐aniline modified silicon dioxide composite with synergistic anticorrosion effect for waterborne epoxy anticorrosive coatings

IN-SITU POLYMERIZATION OF POLYANILINE/CARBON NANOTUBE COMPOSITE

A facile strategy for synthesis of multilayer and conductive organo-silica/polystyrene/polyaniline composite particles.

Preparation and Anticorrosive Performance of the Polyaniline/Strontium Chromate Composites

Preparation and characterization of FeS2/polyaniline composite electrode in lithium-ion battery

Preparation of Doped-Polyaniline and Its Application in Waterborne Anticorrosive and Antistatic Epoxy Coatings

Preparation of an Epoxy/Polyaniline Composite Coating and Its Passivation Effect on Cold Rolled Steel

A Facile and Efficient Route for Coating Polyaniline Onto Positively Charged Substrate