Abstract:Pulverized expandable graphite (pEG) and melamine-formaldehyde (MF) resin core-shell structure particles (pEG@MF) as specific flame retardants for rigid polyurethane foam (RPUF) were synthesized by encapsulating pEG particles with a layer of MF resin via in situ polycondensation. The initial feed weight ratio of pEG and MF prepolymer was found to be the key factor affecting the shell forming process, and the shell growth can be regarded as a combination of raspberry-like' and conventional core-shell' formation mechanisms. With the encapsulation of a well formed MF shell, the expandability of pEG particles was significantly enhanced from 42 mL g(-1) to 76 mL g(-1) and thus the pEG@MF particles showed good flame-retardant performance in RPUF. The RPUF/pEG@MF composites passed the V-0 rate and the limiting oxygen index was remarkably increased from 21 to 28 vol% by adding only 10 wt% pEG@MF particles; both the expandability and available expandable graphite content played an important role in controlling the flame-retardant performance of pEG@MF particles. With a loading of fine sized pEG@MF particles, desirable mechanical and thermal insulation properties of RPUF/pEG@MF composites were achieved by preserving the complete cell structure of RPUF and screening the high thermal conductivity of the pEG particles with the thermally inert MF resin shell. The exciting application of the novel pEG@MF particles indicates that the core-shell structure design of expandable graphite can serve as promising solution for fabricating halogen-free flame-retardant RPUF composites with high performance. (c) 2013 Society of Chemical Industry

Morphology and Property of Expanded Graphite Filled Rigid PU Foam

Structure and Flame-Retardant Actions of Rigid Polyurethane Foams with Expandable Graphite.

Mechanical and Flame‐resistance Properties of Polyurethane‐imide Foams with Different‐sized Expandable Graphite

Expandable Graphite For Halogen-Free Flame-Retardant of High-Density Rigid Polyurethane Foams

Influence of Expandable Graphite on Comprehensive Performance of All-Water Blown Flame Retardant Rigid Polyurethane Foams

Effect of Surface Modification of Montmorillonite on the Properties of Rigid Polyurethane Foam Composites

Flame retardancy of different-sized expandable graphite particles for high-density rigid polyurethane foams

Effect of Expandable Graphite on Properties of Semi-rigid Polyurethane Foam

Flame‐retardant and Mechanical Properties of High‐density Rigid Polyurethane Foams Filled with Decabrominated Dipheny Ethane and Expandable Graphite

Study on Halogen-Free Flame-Retardant High Density Rigid Polyurethane Foam Filled with Expandable Graphite with Different Particle Sizes

Preparation of Boron-coated Expandable Graphite and Its Application in Flame Retardant Rigid Polyurethane Foam

Synthesis and characterization of expandable graphite–poly(methyl methacrylate) composite particles and their application to flame retardation of rigid polyurethane foams

Preparation of a polyurethane‐coated expandable graphite and its flame retardant application in rigid polyurethane foams

Study of different-sized sulfur-free expandable graphite on morphology and properties of water-blown semi-rigid polyurethane foams

Dependence of flame-retardant properties on density of expandable graphite filled rigid polyurethane foam

Effects of Inorganic Fillers on the Flame‐retardant and Mechanical Properties of Rigid Polyurethane Foams

Flame Retardancy of Whisker Silicon Oxide/rigid Polyurethane Foam Composites with Expandable Graphite

Flame retardancy of hollow glass microsphere/rigid polyurethane foams in the presence of expandable graphite

A Facile Strategy To Fabricate Microencapsulated Expandable Graphite As A Flame-Retardant For Rigid Polyurethane Foams

Surface Modification of Expandable Graphite and Its Application in PIR-RPUF

Core-shell Structure Design of Pulverized Expandable Graphite Particles and Their Application in Flame-Retardant Rigid Polyurethane Foams