Abstract:Microencapsulated ammonium polyphosphate (GMAAPP) and microencapsulated expanded graphite (PUEG) were prepared by in situ polymerization with glycidyl methacrylate (GMA) and polyurethane as the shell material respectively. Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and thermogravimetry (TG) were used to characterize GMAAPP and PUEG. The results confirmed the successful fabrication of GMAAPP and PUEG. On this basis, a series of flame-retardant rigid polyurethane foam composites were prepared with GMAAPP and PUEG loading by the one-step water-blown method. The flame retardancy, mechanical properties, thermal insulation, and thermal stability of RPUF/GMAAPP30, RPUF/PUEG30, and RPUF/GMAAPP20/PUEG10 composites were investigated by limiting oxygen index (LOI), Underwriters Laboratories vertical burning test (UL-94), TG, thermal conduction and density test. The results showed that the thermal stability at the high temperature of RPUF composites can be improved by the addition of GMAAPP and PUEG. SEM test confirmed significantly enhanced compatibility between the microencapsulated flame retardant particles and RPUF matrix, which obviously improved the integrity of the cell structure. RPUF/GMAAPP30, RPUF/PUEG30 and RPUF/GMAAPP20/PUEG10 exhibited LOI of 22.3 vol%, 25.3 vol%, 24.6 vol% with all composites passed V-0 rating in UL-94 test. The physical performance test indicated that RPUF/GMAAPP20/PUEG10 exhibited thermal conductivity of 0.0395 W/m·K and compressive strength of 0.292 MPa, which possessed the best comprehensive physical performance. Char residue analysis suggested the combination of GMAAPP and PUEG increased graphitization degree and compactness of char residues for RPUF composites, thus effectively improving the fire safety of the composite.Graphical

Phosphonitrile decorating expandable graphite as a high-efficient flame retardant for rigid polyurethane foams

Enhanced Fire Safety of Rigid Polyurethane Foam via Synergistic Effect of Phosphorus/Nitrogen Compounds and Expandable Graphite

Aluminum Hypophosphite in Combination with Expandable Graphite As A Novel Flame Retardant System for Rigid Polyurethane Foams

Fabrication of Fire Safe Rigid Polyurethane Foam with Reduced Release of CO and NOx and Excellent Physical Properties by Combining Phosphine Oxide-Containing Hyperbranched Polyol and Expandable Graphite

Study on the Flame Retardancy of Rigid Polyurethane Foam with Phytic Acid-Functionalized Graphene Oxide

Synergistic Effect Of Expandable Graphite And Aluminum Hypophosphite On Flame-Retardant Properties Of Rigid Polyurethane Foam

Preparation of flame‐retardant rigid polyurethane foam with bio‐based phosphorus‐containing polyols and expandable graphite

Highly Efficient Flame Retardancy and Fire Spread Behavior of Rigid Polyurethane Foams with extremely low content of Flame Retardant

Synergistic effect of expandable graphite and phenylphosphonic-aniline salt on flame retardancy of rigid polyurethane foam

Flame Retarded Rigid Polyurethane Foams Composites Modified by Aluminum Diethylphosphinate and Expanded Graphite

Phosphorus and Nitrogen-Containing Polyols: Synergistic Effect on the Thermal Property and Flame Retardancy of Rigid Polyurethane Foam Composites

Preparation of a polyurethane‐coated expandable graphite and its flame retardant application in rigid polyurethane foams

Reactive flame-retardants prepared by transesterification between erythritol and dimethyl methyl phosphonate for rigid polyurethane foams

Synergistic fire retardant effect between expandable graphite and ferrocene-based non-phosphorus polymer on polypropylene

Enhanced flame retardancy of rigid polyurethane foam via iron tailings and expandable graphite

Flame retardant rigid polyurethane foam composites based on hexaphenoxycyclotriphosphonitrile: flame retardancy, combustion properties and pyrolysis kinetics

Flame retardant rigid polyurethane foam composites based on microencapsulated ammonium polyphosphate and microencapsulated expanded graphite

Fabrication of Rigid Isocyanate-Based Polyimide Foam Achieved Excellent Use Safety via Synergy between Expandable Graphite and Phosphorus-Containing Polyol

Highly-efficient Reinforcement and Flame Retardancy of Rigid Polyurethane Foam with Phosphorus-Containing Additive and Nitrogen-Containing Compound

Construction and mechanism of efficient flame retardant system for alkali lignin‐enhanced rigid polyurethane foam

Flame retardant and smoke-suppressant rigid polyurethane foam based on sodium alginate and aluminum diethylphosphite