Preparation of Nano-TiO2 via Microemulsion and its Modification with Graphene

Guan-feng TIAN,Hui-e LIU,Shuang CHEN,Chuan-qin DING,Xuan-liang QI
DOI: https://doi.org/10.3969/j.issn.1003-9015.2017.01.019
2017-01-01
Abstract:Nano-titania (TiO2) was prepared by tetrabutyl orthotitanate (Ti(OBu)4) and water in reversed microemulsion systems. Cyclohexane, trimethylstearylammonium chloride (OTAC) andn-butanol were used as oil phase, surfactant and cosurfactant in the microemulsion system, respectively. The molar ratio of water/OTAC was 20. The nano-titania prepared had a diameter of 8~10 nm, which was calcined at different temperatures. Graphene oxide (GO) was prepared from natural flake graphite by Hummers' method, and TiO2-graphene nano-composites (TiO2-RGO) were synthesized by a solvothermal method. The nano-TiO2 and TiO2-RGO composite photocatalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR), Raman spectroscopy (Raman), ultraviolet-visible diffuse reflectance spectroscopy (UV-Vis) and fluorescent spectra. Furthermore, the photocatalytic activity of TiO2 and TiO2-RGO were investigated by photodegradation of 40 mg?L-1 methylene orange (MO) solution under UV light. The results show that TiO2calcined under 450℃ has the highest photocatalytic activity compared with that of other calcination temperature, and 95.3% of initial MO is removed after two hours. In the process of solvothermal reaction, graphene oxide is reduced to graphene due to rapid electronic transmission and excellent adsorption performance of graphene, and the prepared TiO2-RGO nanocomposites exhibit higher photocatalytic activity than pure TiO2, with MO removal rate up to 95.3% after one hour.
What problem does this paper attempt to address?