Preparation of TiO 2 /Ni‐NG Mesoporous Microspheres and Photocatalytic Hydrogen Evolution Properties

Le Zhang,Ke Sun,Xiang Peng,Bingke Li,Xiancai Zeng,Keliang Wu

DOI: https://doi.org/10.1002/cptc.202300232

2024-02-26

ChemPhotoChem

Abstract:Abstract The regulation of surface active sites and structures is a key factor affecting the performance of photocatalysts. In order to prepare monodisperse anatase TiO 2 mesoporous microspheres with higher specific surface area, smaller pore size and particle size, a dual‐surfactant orientation assembly method was selected. Graphene (NG) was selected as a cocatalyst to compound with mesoporous TiO 2 and nickel doping was performed on the cocatalyst to improve the photocatalytic hydrogen production activity of the semiconductor photocatalyst. Through proper regulation and rational design, the semiconductor photocatalyst with desired properties was prepared. SEM characterization of mesoporous titanium dioxide (TiO 2 /Ni‐NG) with graphene cocatalyst proved that TiO 2 nanospheres have good monodispersion, and TiO 2 nanospheres are well supported on graphene cocatalyst. The composite material belonged to mesoporous group with the pore size being mainly distributed between 10–20 nm. The loading of graphene and Ni‐NG cocatalyst increased the absorption band edge by 9 nm and 38 nm, respectively, and the band gap decreased by 0.07 eV and 0.16 eV, respectively. The selection of graphene as cocatalyst improved the hydrogen production activity of photocatalyst and nickel doping was very effective in the modification of graphene. For reaction time of 2.5 h, the H 2 production of TiO 2 /Ni‐NG material reached 1.767 mmol/g which was 7.27 times that of TiO 2 /NG composite material.

chemistry, physical