Abstract:Carbon molecular sieve membrane (CMSM)/paper-like stainless steel fibers (PSSF) has been manufactured by pyrolyzing poly (furfuryl alcohol) (PFA) coated on the metal fibers. PFAwas synthesized using oxalic acid dihydrate as a catalyst and coated on microfibers by dip coating method. For the purpose of investigating the effects of final carbonization temperature, the composites were carbonized between 400°C and 800°C under flowing nitrogen. The morphology and microstructure were examined by X-ray diffraction, Fourier transforms infrared spectroscopy, scanning electron microscopy, thermogravimetric analysis, N2 adsorption and desorption, Raman spectra and X-ray photoelectron spectra. The consequences of characterization showed that the CMSM containing mesopores of 3.9 nm were manufactured. The specific surface area of the CMSM/PSSF fabricated in different pyrolysis temperature varies from 26.5 to 169.1 m2·g-1 and pore volume varies from 0.06 to 0.23 cm3·g-1. When pyrolysis temperature exceeds 600°C, the specific surface, pore diameter and pore volume decreased as carbonization temperature increased. Besides, the degree of graphitization in carbon matrix increased with rising pyrolysis temperature. Toluene adsorption experiments on different structured fixed bed that was padded by CMSM/PSSF and granular activated carbon (GAC) were conducted. For the sake of comparison, adsorption test was also performed on fixed bed packed with GAC. The experimental results indicated that the rate constant κ' was dramatically increased as the proportion of CMCM/PSSF composites increased on the basis of Yoon-Nelson model, which suggested that structured fixed bed padded with CMSM/PSSF composite offered higher adsorption rate and mass transfer efficiency.

Research on the microstructure of porous carbon membranes based on ZSM-5 modified phenolic resin

Synthesis and Physicochemical Characterization of Hierarchical ZSM-5: Effect of Organosilanes on the Catalyst Properties and Performance in the Catalytic Fast Pyrolysis of Biomass

Preparation of Free-Standing High Quality Mesoporous Carbon Membranes

Improved Thermal Stabilities, Ablation and Mechanical Properties for Carbon Fibers/Phenolic Resins Laminated Composites Modified by Silicon-containing Polyborazine

Carbon molecular sieve/ZSM-5 mixed matrix membranes with enhanced gas separation performance and the performance recovery of the aging membranes

Mechanical and Dielectric Properties of Mesoporous Carbon Microsphere/Phenolic Resin Composites

Peparation of Porous Carbon Template with Controllable Channels by Phenolic Resin Pyrolyzing

Highly Proton Conductive and Mechanically Robust SPEEK Composite Membranes Incorporated with Hierarchical Metal–organic Framework/carbon Nanotubes Compound

Preparation of Mesoporous Carbon by Phenol Resin Polymerization-dependent Phase Separation and Pyrolysis

Research on Formation and Gas Separation Performance of Polyetherimide Based Carbon Molecular Sieve Membranes

Enhanced CO2 Adsorption Performance on Hierarchical Porous ZSM-5 Zeolite

Preparation of Paraffin/expanded Vermiculite with Enhanced Thermal Conductivity by Implanting Network Carbon in Vermiculite Layers

Preparation and Mechanism of Interconnected Mesoporous Carbon Monoliths from Phenolic Resin/Ethylene Glycol Mixtures

Pore Structure Control of Mesoporous Carbon Monoliths Derived from Mixtures of Phenolic Resin and Ethylene Glycol

Pyrolysis behavior of the nanoporous phenolic matrix and the resultant microstructure and property evolution in the composites

Preparation of Interconnected Porous Carbon Monoliths by Reaction-Induced Phase Separation and Pyrolysis

Tuning the gas transport performance of carbon molecular sieve membranes by the morphological changes of 6FDA/PMDA-TMMDA precursors

Preparation and characterization of novel carbon molecular sieve membrane/PSSF composite by pyrolysis method for toluene adsorption

Nanocasting Fabrication of Ordered Mesoporous Phenol–formaldehyde Resins with Various Structures and Their Adsorption Performances for Basic Organic Compounds

Effects of pyrolytic carbon on carburization strengthening and corrosion of 3YSZ hollow fiber membranes

Consistent preparation, chemical stability and thermal properties of a shape-stabilized porous carbon/paraffin phase change materials