Preparation and properties of a fluorinated diols modified waterborne hyperbranched polyurethane

Jian-jun YANG,Xiao-hui ZHANG,Qing-yun WU,Ming-yuan WU,Jian-an ZHANG

DOI: https://doi.org/10.3969/j.issn.1001-5922.2016.03.013

2016-01-01

Abstract:The fluorinated diol DEFA with long branched-chain structure was first synthesized. Using DEFA partly instead of small molecule chain extender, the linear polyurethane prepolymer was synthesized, then adding the homemade hyperbranched polyurethane HBPU-0 as the cross-linking agent, and finally reacted with ethylene diamine as chain extender, so the fluorinated diol-modified hyperbranched waterborne polyurethane (FHBPU) emulsion was synthesized. IR spectra results showed that DEFA had been accessed to the hyperbranched polyurethane. After adding DEFA, the heat resistance and hydrophobicity of FHBPU were improved. A series of tests showed that with increasing DEFA content, the particle size of emulsion and tensile strength increased, the elongation at break and water absorption decreased. When DEFA content was 10%, the overall performance of FHBPU was better, in which case its emulsion particle size was 131 nm, the tensile strength was 10.8 MPa, and the elongation at break of 368%, 24 h water absorption was 5.4%.