Abstract:Acetic acid lignin (AAL) obtained from Bagasse was used as a partial substitute of polyols for polyurethane (PU) adhesive due to the presence of reactive sites, i.e. aliphatic and aromatic hydroxyl groups, in its structure. To improve its reactivity, lignin is partly demethylated before the copolymerization with polyisocyanate. The demethylation, catalyzed by hydrobromic acid solution under heating conditions, resulted in a decrease of methoxy groups on the phenyl ring and the increase of phenolic hydroxyl groups. It is found that 120 ℃ is the preferred temperature for the demethylation resulted in a 36.5 % increase in hydroxyl content of lignin up to 5.25 mmol/g. Lignin-based polyurethane adhesives were prepared in two steps including preparing a prepolymer based on mixtures of toluene-2,4-diisocyanate (TDI) and unmodified or demethylated lignin, and then the polymerization was completed by adding polyethylene glycol (PEG). The mass ratio (1:1) of TDI: (lignin + PEG) in the compositions was here investigated. The results indicated that the presence of lignin (with and without demethylation) in polyurethane adhesives increased the glass transition temperature, Young’s modulus, and elongation at break. Particularly, the tensile strength was increased by 15–36 MPa with the addition of 10–30 wt% of lignin. Lignin with higher amount of hydroxyl groups prepared by partly demethylation is better integrated into the three-dimensional cross-linking networks of the covalent polymer as a substitute of polyols. Compared to those PU adhesives based on the raw AAL, the adhesives prepared by demethylated lignin have higher tensile strength and thermal stability. It indicates that the demethylation is effective and it is a good strategy to prepare lignin-based PU adhesive with favorable mechanical properties.

Study on polyurethane adhesives modified by blending lignin

Preparations and Properties of Polyurethane Adhesives Modified by Corn Straw Lignin

Signally improvement of polyurethane adhesive with hydroxy-enriched lignin from bagasse

Study on Polyblending Epoxy Resin Adhesive with Lignin I-curing Temperature

Preparation and Characterization of Lignin-based Polyurethane Prepolymer

Kraft lignin-containing polyurethane adhesives: the role of hydroxypropylation on thermomechanical properties

High-value utilization of hydroxymethylated lignin in polyurethane adhesives.

Polyurethane Adhesives Based on Oxyalkylated Kraft Lignin

Study on Solvent-free Room-temperature Curable Two-compenent PU Structure Adhesive

Facile synthesis of polyester-polyether block copolyols for the sustainable high-performance polyurethane reactive hot melt adhesives

Incorporating Phenolated Lignin into Polyurethane Materials: Impact on Mechanical, Thermal, and Adhesion Performance

Antioxidant and Thermal Stabilization of Polypropylene by Addition of Butylated Lignin at Low Loadings

Use of lignin in polyurethane-based structural wood adhesives

Effect of soft segment molecular weight and NCO:OH ratio on thermomechanical properties of lignin-based thermoplastic polyurethane adhesive

Synthesis and Properties of HBS Lignin Modified Polyurethane

The Preparation of Solvent-Free Polyurethane Laminating Adhesive with Mixed-Polyols

Effect of Enzymatically Hydrolyzed Lignin on the Curing Characteristics of Epoxy Resin/Polyamine Blends

Lignosulfonate-Based Polyurethane Adhesives

The Use of Lignin As Cross-linker for Polyurethane Foam for Potential Application in Adsorbing Materials

Fractionated lignin as a polyol in polyurethane fabrication

Lignin-containing polyurethane elastomers with enhanced mechanical properties via hydrogen bond interactions