Preparation of organic-inorganic intumescent flame retardant with phosphorus, nitrogen and silicon and its flame retardant effect for epoxy resin
Haihua Yu,Yunfei Xia,Xiuhang Xu,Nighat Zarshad,Min Wu,Henmei Ni
DOI: https://doi.org/10.1002/app.49256
IF: 3
2020-01-01
Journal of Applied Polymer Science
Abstract:According to the requirement of fire life cycle assessment (LCA), chitosan ethoxyl urea phosphate (CEUP), an organic-inorganic intumescent flame retardant (IFR) containing phosphorus, nitrogen, and silicon, was synthesized by the reaction of chitosan, phosphorus pentoxide, and urea. FTIR,H-1 NMR, SEM, and XRD were employed to characterize the compounds. As a result, CEUP was successfully prepared with higher thermal stability, favorable to enhance fire resistance. Combined with OMMT, the organic/inorganic IFR was applied as EP flame-retardant agents. The combustion behavior of EP composite was investigated by LOI, UL-94, CCT, SEM, TGA, and TG-IR. It was observed that using 15% CEUP and 3% OMMT (EP3), LOI value reached 34.8% and passed the UL-94 V-0 rating, while THR and TSP of EP composite reduced 65 and 72% compared with pure EP. The char residue of EP composite was up to 22.4%. The thermal decomposition mechanism was traced from 100 to 600 degrees C by TG-IR. It was suggestive that CEUP decomposition commenced at 100 degrees C to create phosphoric acid and sublimation of urea occurred at 300 degrees C. EP3 exhibited a strong thermal stability, namely even at 600 degrees C, the volatile substances were detectable. Dense and expanded carbon layer was confirmed in SEM images.