Abstract:Polyacrylonitrile (PAN) precursor nanofibers are prepared by traditional electrospinning and the centrifugal spinning, respectively. The nanofiber bundles are drawn in hot air with a constant force into 1 and 3 times of the original length. Subsequently, the crystalline structure, orientation, morphology, diameter of PAN nanofibers before and after drawing treatment were characterized by WAXD and SEM. The results show that: (1) the efficiency of centrifugal-electrospinning is far higher (120 times) than that of electrospinning (fluid flow rate of centrifugal-electrospinning: 2 mL/min, fluid flow rate of electrospinning: 1 mL/h). (2) Despite a low crystallinity from centrifugal spinning or electrospinning (the crystallinity of the PAN nanofiber precursor by centrifugal spinning is 25%, while that by electrospinning is 10.6%). PAN precursor nanofibers prepared by centrifugal spinning have certain orientation (60.5%); while those prepared by electrospinning have almost no orientation; (3) Hot-air-drawing with a constant force (1.00 N) contributes to a higher crystallinity (centrifugal spinning: 45.8%, electrospinning: 36.2%) and orientation (centrifugal spinning: 72.5%, electrospinning: 59.8%) for the PAN nanofibers. Moreover, increased drawing temperature and force results in a decrease in the diameter of the PAN nanofiber bundles (the diameter of PAN nanofibers prepared by centrifugal spinning decreases from 675 nm to 510 nm; while that by electrospinning decreases from 460 nm to 355 nm). Compared with the slight effect of the spinning process on crystalline structure and orientation, the hot-air drawing treatment significantly promotes the crystalline and orientation. The centrifugal force is helpful to eliminate the whip phenomenon and to make a full drawing of jet flow, finally leading to a higher certain orientation for the polymer chains of PAN nanofibers.

Preparation of ultrafine polyacrylonitrile nanofibers via composite electrospinning

Refining of polyacrylonitrile nanofiber

Preparation of Polyacrylonitrile and Polystyrene Blend Fibers Through Electrospinning

Preparation and characterization of pan nanofiber via electrostatic spinning

Highly-efficient Fabrication and Crystallinity and Orientation of Polyacrylonitrile Nanofibers

Synthesis of Electrospinning of Polyacrylonitrile/β-Cyclodextrin Composite Nanofiber Membranes and Its Adsorption to Neutral Red

Preparation of porous hollow polyacrylonitrile ultrafine fibers by coaxial electrospinning

Effects of Electrospinning Technological Parameters on Diameter of Polyacrylonitrile Insulation Nano-fiber

PREPARATION OF POROUS POLYACRYLONITRILE ULTRATHIN FIBERS BY ELECTROSPINNING WITH NONSOLVENT INDUCED PHASE SEPARATION

Effect of Fecl3 on the Morphology, Wetting Behavior, and Stabilization/Carbonization of Polyacrylonitrile Nanofibers Prepared by Electrospinning

Preparation and characterization of electrospun Ag/polyacrylonitrile composite nanofibers

Preparation of porous polyacrylonitrile fibers by electrospinning a ternary system of PAN/DMF/H2O

Nano-porous Ultra-High Specific Surface Ultrafine Fibers

Fabrication of Polyacrylonitrile Nanoporous Fibers Via Electrospinning

Preparation and Characterization of PAN-Based Carbon Nanofibers Non-Woven

Preparation of Carbon Nanofiber via Electrospinning of Block Copolymer

Preparation of MWCNTs/PAN Composite Microspheres by Aqueous Deposition Polymerization and Their Electrospun Fibers

Polyacrylonitrile and Carbon Nanofibers with Controllable Nanoporous Structures by Electrospinning

Coaxial Electrospinning with Sodium Dodecylbenzene Sulfonate Solution for High Quality Polyacrylonitrile Nanofibers

SYNTHESIS AND CHARACTERISTICS OF POLYACRYLONITRILE (PAN) NANOFIBER MEMBRANE USING ELECTROSPINNING METHOD

Nanoporous Structured Submicrometer Carbon Fibers Prepared Via Solution Electrospinning of Polymer Blends.