Development of TiO2/MoS2 by Hydrothermal Method for Photocatalytic Hydrogen Generation under Solar Light

Zhong QI,Xi WANG,Laisheng LI,Haitai DONG

DOI: https://doi.org/10.7524/j.issn.0254-6108.2016.05.2015112403

IF: 4.236

2016-01-01

Environmental Chemistry

Abstract:TiO2/MoS2 composite was synthesized by a hydrothermal method.The samples were characterized by X-ray diffraction,transmission electron microscopy,UV-Vis diffuse reflectance spectroscopy,XPS and photoluminescence spectroscopy.the photocatalytic activity of TiO2/MoS2 composite was evaluated by varying the MoS2 content,types of noble mental deposition (such as Pt,Pd,Ru),and types of sacrificial agents.The stability of the catalyst was also investigated.The results suggested that the appropriate content of MoS2 in TiO2/MoS2 is 5 wt％ and the corresponding specific H2 production rate was 776.99.μmol·h-1·g-1,which was 4.92 times and 3.67 times that of TiO2 and commercial P25 respectively.By loading 0.5 wt％ Pd on the TiO2/5 wt％ MoS2,the highest specific hydrogen production rate of 2599 μmol·h-1· g-1 was achieved in 25 vol％ methanol solution.The composite catalyst Pd/(TiO2/MoS2) could produce hydrogen with different electron donors such as methanol,ethanol and lactic acid,and the hydrogen production rate follows the order of methanol＞lactic acid＞ethanol.After 5 cycles of stability test,the hydrogen production rate of Pd/(TiO2/MoS2) preserved 90％.In addition,the mechanism of composite catalyst was also proposed.