Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Experimental Research on the Pitting Corrosion Processes of Q235 Low-carbon Steel Using Acoustic Emission Technical

Acoustic Emission Testing of the Pitting Corrosion of 304 Stainless Steel

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Investigation on Acoustic Emission Characteristics from Corrosion of Conventional Materials of Primary Pipe in Nuclear Power Plants

Monitoring of Laser Quenching of the Carbon Steel by Acoustic Emission

Research on Welding Residual Stress Measurement Using Electromagnetic Acoustic Transducer

Research on Acoustic Emission Detection for Vertical Tank Bottoms under Different Corrosion Conditions

Research on pitting corrosion characteristics of X90 steel based on acoustic emission and electrochemistry methods

Ultrasonic Stress Evaluation on Welded Plates with Lcr Wave

EXPERIMENTAL STUDY OF PIEZOMAGNETISM OF PITTING CORROSIONSTEEL BARS UNDER TENSILE FORCE

Cracking Mechanism of Corroded Reinforced Concrete Column Based on Acoustic Emission Technique

APPLICATION OF ACOUSTIC EMISSION TECHNIQUE IN STUDY OF ELECTROCHEMICAL CORROSION AND STRESS CORROSION CRACKING PROCESSES OF METALS

Comparative Study of Acoustic Emission Characteristics for Intergranular Corrosion of 316L Stainless Steel Parent Material and Weldment

Acoustic Emission Detection During Welding Residual Stresses Release in 2.25cr1mo0.25v Steel Welds

Acoustic Emission Study of Fatigue Crack Propagation in Q345R

Research on Acoustic Emission Characteristics of Metal Material Based on Wavelet Transform

Acoustic Emission During Pitting Corrosion of 304 Stainless Steel

Application of acoustic emission in the study of concrete

Acoustic emission behaviour during the evolution of a single pit on stainless steels

Fracture Toughness Evaluation of 316 LN Stainless Steel and Weld Using Acoustic Emission Technique

The research of acoustic emission techniques for non destructive testing and health monitoring on civil engineering structures