Abstract:Background: Titanium plasma spray coating on polyetheretherketone (PEEK) is a recent innovation to interbody spacer technology. The inherent hydrophobic properties of standard, uncoated PEEK implants can hamper cell attachment and bone healing during fusion. The addition of titanium coating not only offers initial stability due to increased surface roughness but also long-term stability due to bony ongrowth created from osteoconductive microenvironment on the device surface. The previously established hydrophilic and osteophilic properties of commercially pure titanium (CPTi) can potentially provide an ideal environment promoting cell attachment and bony ongrowth when applied at the end plate level of the fusion site. Because the surface material composition and topography is what seems to directly affect cell adhesion, it is important to determine the ideal titanium coating for the highest effectiveness. Purpose: The purpose of the study is to determine whether there is an optimal surface roughness for the titanium coatings and whether different polishing methods have a greater effect than roughness or topography in mediating cell adhesion to the surface. Study design/setting: The study was divided into two phases. In Phase 1, the effects of varying surface roughnesses on identical polishing method were compared. In Phase 2, the effect of varying polishing methods was compared on identical surface roughnesses. Methods: Coating thickness, porosity, and surface roughness were characterized using an optical microscope as per ASTM F 1854 standards. For both phases, PEEK coupons with plasma-sprayed CPTi were used, and human mesenchymal stem cells (hMSCs) at an initial density of 25,000 cells/cm2 were seeded and cultured for 24 hours before fixation in 10% formalin. The cultured hMSCs were visualized by 4',6-diamidino-2-phenylindole (DAPI) staining, a fluorescent stain that binds to the DNA of living cells. Samples were imaged using an environmental scanning electron microscope (eSEM) (Carl Zeiss Microscopy, Thornwood, NY, USA) using a backscattered detector. Results: Image analysis of the CPTi coatings showed uniform and rough surfaces. For Phase 1, roughness was evaluated as fine, medium, and coarse. The eSEM image analysis and cell counting by DAPI demonstrated that hMSCs have a tendency to form stronger adhesion and greater pseudopodia extensions on fine roughness surfaces. Individual hMSCs were seen forming cytoplasmic processes extending across the width of a pore. There was a 4- and 20-fold reduction in adhered hMSCs with an increase to medium and coarse roughnesses, respectively. For Phase 2, studied groups are (1) medium CPTi coating with zirconia polishing, (2) medium CPTi coating with CPTi polishing, and (3) fine CPTi coating with CPTi polishing. The eSEM image analysis and cell counting by DAPI demonstrated that hMSCs have a tendency to form stronger adhesion and greater pseudopodia extensions on Group 3 over the other two groups. There was a twofold reduction in adhered hMSCs on medium roughness relative to fine. No difference in cell adhesion was found between Groups 1 and 2. Individual hMSCs were seen forming cytoplasmic processes extending across the width of a pore. Conclusions: Previously, it was accepted without much scrutiny that surface coatings were beneficial. This study begins to discover that surface topography directly affects the potential for cells to adhere and proliferate and lead to greater surgical efficacy.

Evaluation of the surface alterations and the adhesion strength of human periodontal ligament cells on titanium surface treated by pure titanium and conventional ultrasonic scaler tips

Cell Response of Titanium Implant with a Roughened Surface Containing Titanium Hydride: an in Vitro Study

Functional Behaviour of Human Periodontal Ligament Cells Around Various Dental Implants

Surface Modification And Its Effect On Attachment, Spreading, And Proliferation Of Human Gingival Fibroblasts

Influence on Proliferation and Adhesion of Human Gingival Fibroblasts from Different Titanium Surface Decontamination Treatments: an in Vitro Study

In-Vitro Comparison of Titanium Disc Surface Roughness and Bacterial Colonization after Ultrasonic Instrumentation with Three Different Tips

Micro-/nano-topography of selective laser melting titanium enhances adhesion and proliferation and regulates adhesion-related gene expressions of human gingival fibroblasts and human gingival epithelial cells

Effects of Surface Conditions of Titanium Dental Implants on Bacterial Adhesion

A Comparative Study Of The Influence Of Three Pure Titanium Plates With Different Micro- And Nanotopographic Surfaces On Preosteoblast Behaviors

Human Periodontal Ligament Stem Cells Response to Titanium Implant Surface: Extracellular Matrix Deposition

Fibroblasts and osteoblasts behavior after contact with different titanium surfaces used as implant abutment: An in vitro experimental study

Biological Behavior of Neurally Differentiated Periodontal Ligament Stem Cells on Different Titanium Implant Surfaces

Effect of Er,Cr:YSGG Laser Irradiation on the Surface Modification and Cell Adhesion on Titanium Discs: An In Vitro Study

Influence of eight debridement techniques on three different titanium surfaces: A laboratory study

The biofilm removal effect and osteogenic potential on the titanium surface by electrolytic cleaning: An in vitro comparison of electrolytic parameters and five techniques

In Vitro And In Vivo Evaluation Of Sla Titanium Surfaces With Further Alkali Or Hydrogen Peroxide And Heat Treatment

Ultraviolet Treatment of Titanium to Enhance Adhesion and Retention of Oral Mucosa Connective Tissue and Fibroblasts

Influence of Dental Titanium Implants with Different Surface Treatments Using Femtosecond and Nanosecond Lasers on Biofilm Formation

Effects of TCP/HA-coating Titanium on the Adhesion Behavior of Human Gingival Fibroblasts

Optimizing surface characteristics for cell adhesion and proliferation on titanium plasma spray coatings on polyetheretherketone

Role of Different Scale Structures of Titanium Implant in the Biological Behaviors of Human Umbilical Vein Endothelial Cells