Mechanically Flexible Carbon Aerogel with Wavy Layers and Springboard Elastic Supporting Structure for Selective Oil/Organic Solvent Recovery
Jiran Dong,Jinsong Zeng,Bin Wang,Zheng Cheng,Jun Xu,Wenhua Gao,Kefu Chen
DOI: https://doi.org/10.1021/acsami.1c02394
2021-03-29
Abstract:Even though compressible carbon aerogels are widely studied for oil/organic solvent recovery, it is challenging to simultaneously achieve excellent mechanical performance and recovery efficiency due to the brittleness of the carbon skeleton. Here a novel strategy is proposed to efficiently fabricate a 3D elastic reduced graphene oxide (RGO)-cross-linked carbon aerogel. Notably, cellulose nanocrystals (CNCs) isolated from plant pulp act as an essential component, and prehydrolysis liquor (PHL), an industrial byproduct in the plant pulping process, serves as the adhesion promoter to achieve enhancement of the strength and flexibility of the carbon aerogel. For the first time, all components (pulp and PHL) of the tree were fully exploited to design a carbon aerogel. The formation of wavy carbon layers with springboard elastic supporting microstructure enables mechanical stretch and shrink as well as avoids interfacial collapse during compression. Benefiting from the unique wavy layer structure and strong interaction, the carbon aerogels are ultralight (4.98 mg cm<sup>–3</sup>) and exhibit supercompression (undergoing extreme strain of 95%) and superelasticity (about 100% height retention after 500 cycles at a strain of 50%). Particularly, the carbon aerogel can selectively and quickly adsorb various oily contaminants, exhibiting high oil/organic solvents absorption capacity (reaches up to 276 g g<sup>–1</sup> for carbon tetrachloride) and good recyclability. Finally, practical applications of the carbon aerogel in oil-cleanup and pollution-remediation devices are exhibited. Hence, this versatile and robust functionalized carbon aerogel has promising potential in oil cleanup and pollution remediation.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c02394?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c02394</a>.Experimental section. Photograph of the directional freezing process. Component analysis of xylosugar in PHL. Digital photographs and micromorphology of RGA-6 and RGCA-6. TEM morphologies of RGA, RGCA, and RGCPA<sub>1:1</sub>. Morphologies of GA, GPA, GCA, GCPA<sub>1:1</sub>, GCPA<sub>1:2</sub>, and GCPA<sub>1:4</sub>. The as-prepared RGCPA had low density. XPS high-resolution C 1s spectra of (a) GA, (b) RGA, (c) GCA, (d) RGCA, (e) GCPA<sub>1:2</sub>, and (f) RGCPA<sub>1:2</sub>. Compression performance of RGCPA. Stress remaining in RGA, RGCA, and RGCPA. Nitrogen adsorption–desorption isotherms and pore size distribution of RGCPA<sub>1:2</sub>. Cassie–Baxter nonwetting behavior of RGCPA. Relation between density of different organic solvents and absorption capacity of RGCPA. Adsorption cycle of RGCA for organic solvent. The composition of different suspensions and the corresponding aerogels. Molecular weight of lignin in PHL. Density and porosity of the as-prepared carbon aerogels. Elemental contents of carbon aerogels from elemental analysis. Mechanical properties of the as-prepared carbon aerogels (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c02394/suppl_file/am1c02394_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology