Abstract:The hot compression behavior of as-extruded Mg-0.6Mn-0.5Al-0.5Zn-0.4Ca alloy was studied on a Gleeble-3500 thermal simulation machine. Experiments were conducted at temperatures ranging from 523 to 673 K and strain rates ranging from 0.001 to 1 s −1 . Results showed that an increase in the strain rate or a decrease in deformation temperature led to an increase in true stress. The constitutive equation and processing maps of the alloy were obtained and analyzed. The influence of deformation temperatures and strain rates on microstructural evolution and texture was studied with the assistance of electron backscatter diffraction (EBSD). The as-extruded alloy exhibited a bimodal structure that consisted of deformed coarse grains and fine equiaxed recrystallized structures (approximately 1.57 μm). The EBSD results of deformed alloy samples revealed that the recrystallization degree and average grain size increased as the deformation temperature increased. By contrast, dislocation density and texture intensity decreased. Compressive texture weakened with the increase in the deformation temperature at the strain rate of 0.01 s −1 . Most grains with {0001} planes tilted away from the compression direction (CD) gradually. In addition, when the strain rate decreased, the recrystallization degree and average grain size increased. Meanwhile, the dislocation density decreased. Texture appeared to be insensitive to the strain rate. These findings provide valuable insights into the hot compression behavior, microstructural evolution, and texture changes in the Mg-0.6Mn-0.5Al-0.5Zn-0.4Ca alloy, contributing to the understanding of its processing-microstructure-property relationships.

Influence of Extrusion Temperature on Microstructure and Mechanical Properties of Mg-3Zn-2 .5Al-2 .5 Ca Alloy

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Effect of extrusion temperature on microstructure, mechanical properties, and deformation mechanism of Mg-2.5Er-0.6Zr alloy

Effect of Hot Extrusion on Microstructure, Texture, and Mechanical Properties of Mg-Zn-Mn-0.5Ca Alloy

Microstructure and tensile properties of a low-alloyed magnesium alloy: effect of extrusion temperature

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructure evolution, strengthening mechanisms and deformation behavior of high-ductility Mg−3Zn−1Y−1Mn alloy at different extrusion temperatures

Effect of Extrusion Process on Microstructure, Corrosion Properties, and Mechanical Properties of Micro-Alloyed Mg–Zn–Ca–Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Nd-Y-Zr-Ca Alloy

Microstructure, Non-Basal Texture and Strength-Ductility of Extruded Mg-6Bi-3Zn Alloy

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Microstructure modification and precipitation strengthening for Mg–6Zn–1Mn–4Sn–0.5Ca through extrusion and aging treatment

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Hot Extrusion Effect on the Microstructure and Mechanical Properties of a Mg–Y–Nd–Zr Alloy

Influence of Extrusion Ratio on Microstructure and Tensile Properties of Mg–Gd–Y–Zn–Zr Alloy

Effect of Zn/Mg Ratio on Microstructure and Properties of Cold Extruded Al-xZn-2.4Mg-0.84Cu-0.2Zr-0.25Ti Aluminum Alloy

Effect of Artificial Cooling Extrusion on Microstructure and Mechanical Properties of Mg–Zn–Y Alloys

Microstructure and properties of biomedical Mg-Zn-Ca alloy at different extrusion temperatures

EFFECT OF Zr, Zn AND Cu ADDITIONS ON ELEVATED-TEMPERATURE MECHANICAL PROPERTIES OF AS-EXTRUDED Mg-3Sn-1Ca ALLOY

Hot deformation behavior of novel high-strength Mg-0.6Mn-0.5Al-0.5Zn-0.4Ca alloy