Abstract:This work aimed at evaluating the effect of nickle (Ni) dopant on the catalytic performance of Co3 O4 catalyst for abatement of harmful carbon monoxide (CO), a resistance toward sintering and durability of catalytic activity were also pursued. Choose the Co(NO3 )2 ×6H2 O(aq) as precursor and NaOH as precipitant to prepare cobalt oxide (Co3 O4 ) with precipitation method, then calcined at 300 and 500 °C, separately (named as C3 and C5). The Ni dopant (0.1 ~ 5 wt%) was added by deposited precipitation through Ni(NO3)2 ×6H2 O(aq) with drop wisely added NaOH(aq) into suspended Co3 O4 solution, then put the NaOCl for oxidation to obtain series 0.1%Ni-Co3 O4 , 0.2%Ni-Co3 O4 , 1%Ni-Co3 O4 and 5%Ni-Co3 O4 catalysts. All catalysts were characterized through BET, XRD, TEM/SEM, Raman, ICP and TPR instruments, and evaluated the catalytic performance of CO oxidation with a self-devised fluidized micro-reactor. It was observed that the calcination temperature and loading of dopant remarkably influenced the physicochemical characteristics and catalytic performance of the catalysts. Preferential catalyst was obtained for calcination at 300 °C and loading of Ni dopant below 1%. The doping of Ni on the surface of Co3 O4 enhanced the performance due to the inducing of synergistic effect between Co3 O4 and NiO, while the excessive NiO incorporated to the surface constrained the activity due to the abundant NiO on the surface, overlaying the active sites caused the decreasing of surface area and reducible capacity. Among these series Ni-Co3 O4 catalysts, the 0.2%Ni-Co3 O4 (C3) catalyst behaved an eminent activity with T50 of 98 °C and durability without apparent deactivation for 50 hr reaction at 125 °C. The excellent performance is primarily attributed to the synergistic effect and formation of NiCo2 O4 composite oxide.

Effect of Fe-Ni bimetal oxides with different element molar ratios on catalytic activity

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Effect of the Composition and Surface Functional Groups of Fe-Ni Bimetal Oxides Catalysts in Catalytic Ozonation Process

High Catalytic Activity of Magnetic FeOx/NiOy/SBA-15: the Role of Ni in the Bimetallic Oxides at the Nanometer Level

Correlating C═C, C═O, and C═N Hydrogenation Activity with Hydrogen Binding Energies on Ni–Fe Bimetallic Catalysts

Investigation of Fe-Ni Mixed-Oxide Catalysts for the Reduction of NO by CO: Physicochemical Properties and Catalytic Performance

Promotional effect of Fe on performance of Ni/SiO2 for deoxygenation of methyl laurate as a model compound to hydrocarbons

Effect of Oxide Support on Catalytic Performance of FeNi‐based Catalysts for CO2‐assisted Oxidative Dehydrogenation of Ethane

Effective Regulation Mechanisms of Fe-Ni(oxy)hydroxide: Ni-rich Heteroatomic Bonding (Ni-O-fe-o-ni) is Essential

Preparation and Performance of Supported Bimetallic Catalysts for Hydrogen Production from Ammonia Decomposition by Plasma Catalysis

Preparation of Bimetal-Based FeNi-N/C Catalyst and Its Electrocatalytic Oxygen Reduction Performance

ABATEMENT OF HARMFUL CARBON MONOXIDE OVER THE NICKLE DOPED CO3 O4 CATALYST

Catalytic Oxidation of Nitric Oxide over Mn–Fe Metal Oxides Catalysts

Electronic Metal-Support Interactions in Pt/FeOx Nanospheres for CO Oxidation

CeO2 nanorods supported M-Co bimetallic oxides (M = Fe, Ni, Cu) for catalytic CO and C3H8 oxidation

Mesoporous NiO–CeO2 Catalysts for CO Oxidation: Nickel Content Effect and Mechanism Aspect

Role of Ptnc-FeOx metal-oxide interface in enhancing the catalytic activity for CO oxidation

Ni/Fe Ratio Dependence of Catalytic Activity in Monodisperse Ternary Nickel Iron Phosphide for Efficient Water Oxidation

Effect of Ni on the catalytic performance of Pt/γ-Al2 O3 in methylcyclohexane dehydrogenation

Effect of Molar Ratio of Citric Acid to Metal Nitrate on the Structure and Catalytic Activity of NiO Nanoparticles

Effects of Composite Oxide Supports on Catalytic Performance of Ni-based Catalysts for CO Methanation