Optimising Dopants and Properties in BiMeO3 (me = Al, Ga, Sc, Y, Mg2/3Nb1/3, Zn2/3Nb1/3, Zn1/2Ti1/2) Lead-Free BaTiO3-BiFeO3 Based Ceramics for Actuator Applications
Shunsuke Murakami,Nihal Thafeem Ahmed Faheem Ahmed,Dawei Wang,Antonio Feteira,Derek C. Sinclair,Ian M. Reaney
DOI: https://doi.org/10.1016/j.jeurceramsoc.2018.05.019
IF: 5.7
2018-01-01
Journal of the European Ceramic Society
Abstract:A crystallochemical framework is proposed based on electronegativity difference (e(n)) and tolerance factor (t) to optimise the BiMeO3 dopants and therefore the piezoelectric and high-field strain response in BaTiO3-BiFeO3 based ceramics. Compositions in the series 0.05Bi(Me)O-3 -0.25BaTiO(3)-0.7BiFeO(3) (BMe-BT-BF, Me: Y, Sc1/2Y1/2, Mg2/3Nb1/3, Sc, Zn2/3Nb1/3, Zn1/2Ti1/2, Ga, and Al) were fabricated using solid state synthesis and furnace cooled. Scanning electron microscopy and X-ray diffraction revealed that only Bi(Mg-2/3 Nb-1/3)O-3 and BiScO3 dopants, which lie in a narrow range of e(n), vs. t, form homogeneous ceramics, free from secondary phases reflected in their superior piezoelectric coefficients (d(33) similar to 145 pC/N). All other BiMeO3 additions exhibited either secondary phases (Y) and/or promoted a two-phase perovskite matrix (Zn, Ga and Al). The promising initial properties of BiScO3 doped compositions prompted further studies on 0.05BiScO(3)-(0.95-x)BaTiO3-(x) BiFeO3 (BS-BT-BF, x = 0.55, 0.60, 0.625, 0.65, and 0.70) ceramics. As x increased the structure changed from predominantly pseudocubic to rhombohedral, resulting in a transition from a relaxor-like to ferroelectric response. The largest d(33)* (465 pm/V) was achieved for x = 0.625 under 5 kV/mm at the crossover from relaxor to ferroelectric behaviour. BS-BT-BF with x = 0.625 showed > 0.3% strain under 6 kV/mm up to 175 degrees C, demonstrating its potential for actuator applications.