Electron-Injection-Engineering Induced Phase Transition toward Stabilized 1T-MoS 2 with Extraordinary Sodium Storage Performance
Hanna He,Xiaolong Li,Dan Huang,Jinyi Luan,Sailin Liu,Wei Kong Pang,Dan Sun,Yougen Tang,Wenzheng Zhou,Lirong He,Chuhong Zhang,Haiyan Wang,Zaiping Guo
DOI: https://doi.org/10.1021/acsnano.1c01518
IF: 17.1
2021-05-10
ACS Nano
Abstract:Phase transition engineering, with the ability to alter the electronic structure and physicochemical properties of materials, has been widely used to achieve the thermodynamically unstable metallic phase MoS<sub>2</sub> (1T-MoS<sub>2</sub>), although the complex operating conditions and low yield of previous strategies make the large-scale fabrication of 1T-MoS<sub>2</sub> a big challenge. Herein, we report a facile electron injection strategy for phase transition engineering and fabricate a composite of conductive TiO chemically bonded to 1T-MoS<sub>2</sub> nanoflowers (TiO-1T-MoS<sub>2</sub> NFs) on a large scale. The underlying mechanism analysis reveals that electron-injection-engineering triggers a reorganization of the Mo 4d orbitals and results in a 100% phase transition of MoS<sub>2</sub> from 2H to 1T. In the TiO-1T-MoS<sub>2</sub> NFs composite, the 1T-MoS<sub>2</sub> demonstrates a higher electronic conductivity, a lower Na<sup>+</sup> diffusion barrier, and a more restricted S release than 2H-MoS<sub>2</sub>. In addition, conductive TiO bonding successfully resolves the stability challenge of the 1T phase. These merits endow TiO-1T-MoS<sub>2</sub> NFs electrodes with an excellent rate capability (650/288 mAh g<sup>–1</sup> at 50/20 000 mA g<sup>–1</sup>, respectively) and an outstanding cyclability (501 mAh g<sup>–1</sup> at 1000 mA g<sup>–1</sup> after 700 cycles) in sodium ion batteries. Such an improvement signifies that this facile and scalable phase-transition engineering combined with a deep mechanism analysis offers an important reference for designing advanced materials for various applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c01518?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c01518</a>.XRD pattern, SEM and TEM images for TiO<sub>2</sub>–MoS<sub>2</sub> NFs precursor. Thermogravimetry results for melamine. XRD patterns for TiO NPs, 2H-MoS<sub>2</sub>, TiO-1T-MoS<sub>2</sub> NFs, and TiO<sub>2</sub>-2H-MoS<sub>2</sub> NFs. Schematic diagram of the preparation of TiO<sub>2</sub>-2H-MoS<sub>2</sub> NFs. The splitting of the degenerate Mo 4d orbitals for 2H phase and 1T phase MoS<sub>2</sub> with and without extra electron donation. SEM and TEM results for TiO<sub>2</sub>-2H-MoS<sub>2</sub> NFs. S 2p XPS spectra for 2H-MoS<sub>2</sub>, TiO<sub>2</sub>-2H-MoS<sub>2</sub> NFs, and TiO-1T-MoS<sub>2</sub> NFs. Electrochemical performance of TiO NPs. Charge–Discharge profiles and CV results for 2H-MoS<sub>2</sub>, TiO<sub>2</sub>-2H-MoS<sub>2</sub> NFs, and TiO-1T-MoS<sub>2</sub> NFs. <i>In operando</i> XRD data for TiO-1T-MoS<sub>2</sub>. Ti 2p XPS spectra for TiO-1T-MoS<sub>2</sub> electrode after different cycles. TDOS spectra for bulk 2H-MoS<sub>2</sub> and 1T-MoS<sub>2</sub>. PDOS spectra for bulk TiO<sub>2</sub> and TiO. DFT calculation models. The binding energy of different calculation structures (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c01518/suppl_file/nn1c01518_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology